Effect of Composition Gradient on Microstructure and Properties of Laser Deposition TC4/TC11 Interface

IMR OpenIR

	Effect of Composition Gradient on Microstructure and Properties of Laser Deposition TC4/TC11 Interface
其他题名	Effect of Composition Gradient on Microstructure and Properties of Laser Deposition TC4/TC11 Interface
	He Bo; Xing Meng; Yang Guang; Xing Fei; Liu Xiangyu
	2019
发表期刊	ACTA METALLURGICA SINICA
ISSN	0412-1961
卷号	55 期号:10 页码:1251-1259
摘要	In recent years, gradient composites have been increasingly used in life and industry. The rapid development of laser deposition manufacturing (LDM) technology realizes the manufacturing of dissimilar-metal gradient composite structure used for main bearing component. In this work, laser deposited TC4/TC11 gradient composite structures are taken as the research objects. Since there are few studies on TC4/TC11 titanium alloy, this work focuses on the effect of heat treatment on the microstructures and properties of TC4/TC11 titanium alloy, providing the basis to improve the quality and serving life of laser deposited gradient composite structure. Based on comparative study on the microstructures, residual static performances, tensile fractures, room temperature abrasion results and microhardnesses of laser deposition TC4/TC11 titanium alloy specimens with different composition gradients under different heat treatments, the ways to improve the laser deposition TC4/TC11 titanium alloy microstructure and the comprehensive mechanical properties were explored. Results show that when the temperature of solution and ageing treatment rises to 970 degrees C, the length-width ratio of alpha laths of TC4/TC11 titanium alloy is less than that of the other heat treatment samples. The globular alpha phase and the short bar alpha phase are significantly increased. The microstructure of the three-layer transition zone is more uniform and orderly, and the transition interface almost disappears. With the increase of the number of transition layers, the strength and plasticity of solution and ageing samples with different component gradients are increased. The frictional coefficient curve of sample with 1 transition layer is similar to that of the sample with 3 transition layers. The friction coefficient of the sample with the transition layer of 0 is relatively small. The wear mechanism of solution and ageing samples with different component gradients are mainly lamination wear and adhesive wear. From the as-deposited state to the stress relieved and finally to the ageing state of solid solution, the corresponding hardness of the sample with different component gradients increases successively.
关键词	TC4 TITANIUM-ALLOY MECHANICAL-PROPERTIES HEAT-TREATMENT COOLING RATE TI3AL/TC11 EVOLUTION laser deposition manufacturing titanium alloy heat treatment microstructure property
收录类别	CSCD
语种	英语
资助项目	[National Key Research and Development Program of China] ; [Civil Aircraft Special Scientific Research Project of Ministry of Industry and Information Technology] ; [Scientific Research Project of Liaoning Provincial Department of Education] ; [Open Fund of Key Laboratory of Fundamental Science for National Defence of Aeronautical Digital Manufacturing Process]
CSCD记录号	CSCD:6590508
引用统计	被引频次：4[CSCD] [CSCD记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/151624
专题	中国科学院金属研究所
作者单位	中国科学院金属研究所
推荐引用方式 GB/T 7714	He Bo,Xing Meng,Yang Guang,et al. Effect of Composition Gradient on Microstructure and Properties of Laser Deposition TC4/TC11 Interface[J]. ACTA METALLURGICA SINICA,2019,55(10):1251-1259.
APA	He Bo,Xing Meng,Yang Guang,Xing Fei,&Liu Xiangyu.(2019).Effect of Composition Gradient on Microstructure and Properties of Laser Deposition TC4/TC11 Interface.ACTA METALLURGICA SINICA,55(10),1251-1259.
MLA	He Bo,et al."Effect of Composition Gradient on Microstructure and Properties of Laser Deposition TC4/TC11 Interface".ACTA METALLURGICA SINICA 55.10(2019):1251-1259.