La1-xYxNi4.8Mn0.2合金的贮氢性能研究
Alternative TitleHydrogen Storage Properties of La1-xYxNi4.8Mn0. 2 Alloys
李慎兰; 程宏辉; 邓小霞; 陈伟; 陈德敏; 杨柯
2008
Source Publication西安交通大学学报
ISSN0253-987X
Volume42.0Issue:003Pages:359-363
Abstract研究了w(Y)变化对La1-xYxNi4.8Mn0.2(x=0.2,0.5)贮氢合金的晶胞参数、热力学性能、动力学性能和平台特性,及其抗粉化性能的影响.研究结果表明,随着w(Y)的增加,吸放氢平台压力升高,平台斜率增大,滞后因子略有增加,贮氢容量减少,吸氢动力学性能略有下降,但抗粉化性能却明显提高.研究发现,X射线衍射图谱中(111)主峰半高宽值与合金的滞后因子具有相同的变化趋势.
Other AbstractThe influences of Y content x on the lattice parameters, thermodynamic properties, absorption kinetics, plateau characters and pulverization resistance of La1-x YxNi4.8 Mn0.2 (x = 0.2, 0.5) alloys are investigated. The experimental results show that with the increasing Y content, the absorption/desorption plateau pressure, the hysteresis factor and the plateau slope are enhanced, the absorption kinetics is reduced slightly and the hydrogen intake capacity is impaired while the pulverization resistance is improved obviously. It is found that the hysteresis factor has the same variation trend as full width at half maximum of (111) peak in the XRD patterns.
Keyword贮氢合金 动力学 抗粉化性能
Indexed ByCSCD
Language中文
CSCD IDCSCD:3223913
Citation statistics
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/152115
Collection中国科学院金属研究所
Affiliation中国科学院金属研究所
Recommended Citation
GB/T 7714
李慎兰,程宏辉,邓小霞,等. La1-xYxNi4.8Mn0.2合金的贮氢性能研究[J]. 西安交通大学学报,2008,42.0(003):359-363.
APA 李慎兰,程宏辉,邓小霞,陈伟,陈德敏,&杨柯.(2008).La1-xYxNi4.8Mn0.2合金的贮氢性能研究.西安交通大学学报,42.0(003),359-363.
MLA 李慎兰,et al."La1-xYxNi4.8Mn0.2合金的贮氢性能研究".西安交通大学学报 42.0.003(2008):359-363.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[李慎兰]'s Articles
[程宏辉]'s Articles
[邓小霞]'s Articles
Baidu academic
Similar articles in Baidu academic
[李慎兰]'s Articles
[程宏辉]'s Articles
[邓小霞]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[李慎兰]'s Articles
[程宏辉]'s Articles
[邓小霞]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.