| The Aging Behavior of Aluminum-Lithium Alloy 2A97 | |
| 其他题名 | The Aging Behavior of Aluminum-Lithium Alloy 2A97 |
| Yuan Zhishan1; Wu Xiuliang2; Lu Zheng2; Xie Youhua2; Dai Shenglong2; Liu Changsheng1 | |
| 2008 | |
| 发表期刊 | RARE METAL MATERIALS AND ENGINEERING
 |
| ISSN | 1002-185X |
| 卷号 | 37期号:11页码:1898-1902 |
| 摘要 | The evolution of microstructures and properties of aged 2A97 alloy at 165 degrees C after quenching, and at 135 degrees C after quenching and 4% plastic deformation for various times were investigated. The results show that theta ''/theta' and delta' phases are the main strengthening phases of aged alloy at 165 degrees C for 18 h after quenching, which shows high tensile strength and ductility resulting from increasing amount of T(1) phase distributed heterogeneously in matrix. With increasing aging time at 165 degrees C, the number density of theta ''/theta', T(1), and delta' increase, and the length of T(1) decreases, while the length of theta ''/theta' increases. Stretch before aging fines the size of theta ''/theta' and T(1), and stimulates the precipitation and uniform distribution of them, so it yields higher strength for the alloy aged at 135 degrees C for 36 h after quenching and stretch, which is 441 MPa, 519 MPa, and 7.4% for sigma(0.2), sigma(b), and sigma(5), respectively, than the alloy aged at 165 degrees C after quenching. |
| 关键词 | ULTRA-HIGH-STRENGTH AG-MG ALLOY ZR ALLOY aging reversion 2A97 aluminum-lithium alloy DSC XRD |
| 收录类别 | CSCD |
| 语种 | 英语 |
| CSCD记录号 | CSCD:3474901 |
| 引用统计 | |
| 文献类型 | 期刊论文 |
| 条目标识符 | http://ir.imr.ac.cn/handle/321006/152436 |
| 专题 | 中国科学院金属研究所 |
| 作者单位 | 1.中国科学院金属研究所 2.Beijing Institute Aeronaut Mat, Beijing 100095, Peoples R China |
| 推荐引用方式 GB/T 7714 | Yuan Zhishan,Wu Xiuliang,Lu Zheng,et al. The Aging Behavior of Aluminum-Lithium Alloy 2A97[J]. RARE METAL MATERIALS AND ENGINEERING,2008,37(11):1898-1902. |
| APA | Yuan Zhishan,Wu Xiuliang,Lu Zheng,Xie Youhua,Dai Shenglong,&Liu Changsheng.(2008).The Aging Behavior of Aluminum-Lithium Alloy 2A97.RARE METAL MATERIALS AND ENGINEERING,37(11),1898-1902. |
| MLA | Yuan Zhishan,et al."The Aging Behavior of Aluminum-Lithium Alloy 2A97".RARE METAL MATERIALS AND ENGINEERING 37.11(2008):1898-1902. |
| 条目包含的文件 | 条目无相关文件。 | |||||
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论