| 具有纳米结构表层的纯铁和38CrMoAl钢的渗氮 | |
| 其他题名 | Nitriding Iron and 38CrMoAl Steel with a Nanostructured Surface Layer |
| Tong Weiping1; Tao Nairong1; Wang Zhenbo1; Lu Jian2; Lu Ke1 | |
| 2005 | |
| 发表期刊 | 中国科学院研究生院学报
 |
| ISSN | 1002-1175 |
| 卷号 | 22.0期号:002页码:230-238 |
| 摘要 | 通过表面机械研磨技术(SMAT)，在纯铁和38CrMoAl钢样品表面产生大量的塑性应变，致使其表层晶粒细化至纳米量级．随后的气体渗氮实验表明，纳米纯铁和38CrMoAl钢发生渗氮反应的温度大大低于传统粗晶材料(>500℃)，分别降至约300℃和400℃．这种低温渗氮过程不仅有利于降低渗氮工件的变形和能耗，也为选择性渗氮技术的实现提供了新途径． |
| 其他摘要 | The microstructure of the surface layer on a pure iron and a 38CrMoAl steel samples was refined into the nanometer scale by means of the surface mechanical attrition treatment (SMAT) that generates repetitive severe plastic deformation in the surface layer. The subsequent nitriding kinetics of the SMAT samples with a nanostructured surface layer is greatly enhanced so that the nitriding temperatures can be reduced to 300℃ for iron and about 400℃ for 38CrMoAl steel, respectively, which are much lower than the conventional nitriding temperatures (above 500℃). The novel nitriding process not only facilitates reduction of torsion of the treated samples, but also provides a new approach for selective surface reactions of solids. |
| 关键词 | 纳米材料 38CrMoAl钢 铁 渗氮 表面机械研磨 |
| 收录类别 | CSCD |
| 语种 | 中文 |
| CSCD记录号 | CSCD:2022762 |
| 引用统计 | |
| 文献类型 | 期刊论文 |
| 条目标识符 | http://ir.imr.ac.cn/handle/321006/153238 |
| 专题 | 中国科学院金属研究所 |
| 作者单位 | 1.中国科学院金属研究所 2.特鲁瓦工程技术大学 |
| 推荐引用方式 GB/T 7714 | Tong Weiping,Tao Nairong,Wang Zhenbo,等. 具有纳米结构表层的纯铁和38CrMoAl钢的渗氮[J]. 中国科学院研究生院学报,2005,22.0(002):230-238. |
| APA | Tong Weiping,Tao Nairong,Wang Zhenbo,Lu Jian,&Lu Ke.(2005).具有纳米结构表层的纯铁和38CrMoAl钢的渗氮.中国科学院研究生院学报,22.0(002),230-238. |
| MLA | Tong Weiping,et al."具有纳米结构表层的纯铁和38CrMoAl钢的渗氮".中国科学院研究生院学报 22.0.002(2005):230-238. |
| 条目包含的文件 | 条目无相关文件。 | |||||
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论