模拟燃烧环境介质和温度对不锈钢表面氧化物形态的影响研究

IMR OpenIR

	模拟燃烧环境介质和温度对不锈钢表面氧化物形态的影响研究
其他题名	Oxidation Behavior of Stainless Steel 1Cr11Ni2W2MoV in a Simulated Kerosene Combustion Environment
	谢冬柏 1; 洪昊 2; 王文 3; 彭晓 1; 多树旺 2
	2020
发表期刊	中国腐蚀与防护学报
ISSN	1005-4537
卷号	40.0 期号:004 页码:358-366
摘要	研究了耐热不锈钢1Cr11Ni2W2MoV在600,700和800℃空气和模拟煤油燃烧环境中的氧化行为,对表面生成的氧化物进行了表征,并讨论了环境介质对耐热不锈钢高温氧化行为的影响机制。结果表明:1Cr11Ni2W2MoV耐热钢在热空气中表面生成的氧化膜完整致密,表现出优良的抗氧化性能;而在模拟煤油燃烧环境中表面形成了疏松的氧化膜,并出现了瘤状氧化物,加速了不锈钢中Cr的消耗,明显降低了表面氧化膜的保护性。
其他摘要	Metallic materials exposed to fire scenes are usually subjected to high temperature oxidation,of which the atmosphere composition and temperature have been considered as vital parameters.In this study,the high temperature oxidation behavior of 1Cr11Ni2W2MoV stainless steel in air and simulated kerosene-combustion atmosphere at 600,700 and 800℃were studied by means of visual analysis and micro-structural observation of the formed oxide scale.The results show that the 1Cr11Ni2W2MoV possessed good oxidation resistance and the scales primarily remained continuous and well adherent to the substrate in air.Whilst,the presence of kerosene combustion products apparently increased the consumption of Cr element,reduced the adhesion of oxide scale and hence decreased the oxidation resistance of the steel.Additionally,the combustion products of kerosene resulted in the formation of nodular oxides in the formed scale.Therefore,the combustion of kerosene in fire scene could increase the oxidation rate of 1Cr11Ni2W2MoV,which are expected to offer complementary insight into reconstruction of fire scene.
关键词	燃烧环境火灾调查 1Cr11Ni2W2MoV 氧化物高温腐蚀
收录类别	CSCD
语种	中文
CSCD记录号	CSCD:6755032
引用统计
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/153990
专题	中国科学院金属研究所
作者单位	1.南昌航空大学 2.江西科技师范大学 3.中国科学院金属研究所
推荐引用方式 GB/T 7714	谢冬柏,洪昊,王文,等. 模拟燃烧环境介质和温度对不锈钢表面氧化物形态的影响研究[J]. 中国腐蚀与防护学报,2020,40.0(004):358-366.
APA	谢冬柏,洪昊,王文,彭晓,&多树旺.(2020).模拟燃烧环境介质和温度对不锈钢表面氧化物形态的影响研究.中国腐蚀与防护学报,40.0(004),358-366.
MLA	谢冬柏,et al."模拟燃烧环境介质和温度对不锈钢表面氧化物形态的影响研究".中国腐蚀与防护学报 40.0.004(2020):358-366.