Y对Fe50-xMo14Cr15C15B6Yx非晶合金非晶形成能力及耐腐蚀性能的影响

IMR OpenIR

	Y对Fe50-xMo14Cr15C15B6Yx非晶合金非晶形成能力及耐腐蚀性能的影响
其他题名	Effects of Yttrium on the Glass-Forming Ability and Corrosion Resistance of Fe50-xMo14Cr15C15B6Yx Amorphous Alloys
	周正; 王鲁; 王富耻; 张海峰; 程焕武; 柳彦博; 徐赛华
	2008
发表期刊	北京理工大学学报
ISSN	1001-0645
卷号	28.0 期号:005 页码:455-458
摘要	采用单辊法制备Fe50-xMo14Cr15C15B6Yx（x=0,2）非晶合金条带,利用X射线衍射、差热分析、透射电镜和电化学极化曲线方法对非晶合金的结构、非晶形成能力（GFA）、热稳定性、晶化过程及腐蚀行为等进行了研究和表征.结果表明：Fe50-xMo14Cr15C15B6Yx合金能够形成非晶合金,随着Y元素的添加,其非晶相含量、非晶形成能力及热稳定性显著提高.晶化处理后,析出的主要晶体相为α-Fe,Fe23B6,Cr23C6和Fe3Mo3C等.Fe50-xMo14Cr15C15B6Yx非晶合金在质量分数为3.5%NaCl水溶液中呈现出极强的耐腐蚀能力,远优于常用耐蚀不锈钢Cr18Ni9Ti,并且随着Y元素的加入,非晶合金的耐腐蚀能力进一步提高,具有更宽的钝化区间及更低的腐蚀电流密度.
其他摘要	Fe50-xMo14Cr15C15B6Yx（x=0,2） amorphous alloy ribbons were prepared by single roller method.The structures,glass-forming ability（GFA）,thermal stability,crystallization process and corrosion behavior of the amorphous alloys were investigated by means of X-ray diffraction,differential scanning calorimetry,transition electron microscopy and potentiodynamic polarization experiments.The results showed that the Fe50-xMo14Cr15C15B6Yx（x=0,2） alloys can be prepared into amorphous alloy ribbons.The amorphous content,GFA and thermal stability of the amorphous alloys are extremely enhanced with yttrium addition.The predominant crystalline phases precipitated after the crystallization process are α-Fe,Fe23B6,Cr23C6 and Fe3Mo3C.The amorphous alloys exhibit higher corrosion resistance in 3.5%NaCl aqueous solution compared with stainless steel Cr18Ni9Ti,and show wider passive region and lower passive current density with yttrium addition.
关键词	氨基树脂型膨胀阻燃剂的合成及应用研究Fe基非晶合金非晶形成能力热稳定性耐腐蚀性
收录类别	CSCD
语种	中文
CSCD记录号	CSCD:3288000
引用统计	被引频次：3[CSCD] [CSCD记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/154133
专题	中国科学院金属研究所
作者单位	中国科学院金属研究所
推荐引用方式 GB/T 7714	周正,王鲁,王富耻,等. Y对Fe50-xMo14Cr15C15B6Yx非晶合金非晶形成能力及耐腐蚀性能的影响[J]. 北京理工大学学报,2008,28.0(005):455-458.
APA	周正.,王鲁.,王富耻.,张海峰.,程焕武.,...&徐赛华.(2008).Y对Fe50-xMo14Cr15C15B6Yx非晶合金非晶形成能力及耐腐蚀性能的影响.北京理工大学学报,28.0(005),455-458.
MLA	周正,et al."Y对Fe50-xMo14Cr15C15B6Yx非晶合金非晶形成能力及耐腐蚀性能的影响".北京理工大学学报 28.0.005(2008):455-458.