超厚板TC4钛合金电子束焊接接头应力腐蚀敏感性

IMR OpenIR

	超厚板TC4钛合金电子束焊接接头应力腐蚀敏感性
其他题名	Stress corrosion crack sensitivity of ultra-thick TC4 titanium alloy electron beam welding joints
	房卫萍 1; 肖铁 2; 张宇鹏 1; 徐望辉 1; 易耀勇 1
	2019
发表期刊	焊接学报
ISSN	0253-360X
卷号	40.0 期号:012 页码:121-128
摘要	针对100 mm超厚板TC4钛合金电子束焊接接头,采用慢应变速率拉伸方法评价接头在人造海水中的应力腐蚀敏感性,分析接头的显微组织和断口形貌,对接头的腐蚀机制进行研究.结果表明,室温条件下应变速率为ε=1×10-6 s-1时,母材在海水中未表现出应力腐蚀敏感性;焊缝上部、中部和下部具有轻微应力腐蚀敏感性.焊缝在海水中发生阳极溶解,产生氢吸附,导致裂纹的萌生.同时氢扩散诱导α’相界及α’相内发生位错塞积,进而使裂纹在更低的应力水平下发生扩展.
其他摘要	Slow strain rate tensile method was adopted to evaluate the stress corrosion crack(SCC) sensitivity of 100 mm ultra-thick TC4 titanium alloy electron beam welded(EBW) joints under artificial seawater. The corrosion mechanism was studied by observing the microstructure and fracture morphology of the joint. The results showed that the base metal have no SCC sensitivity in seawater. However, the upper, middle and lower parts of the weld showed slight SCC sensitivity at room temperature under the condition of strain rate ε = 1 × 10-6 s-1. In seawater, anodic dissolution accursed in the weld metal, which increased the Ti ion concentration in the solution at the crack tip, then, H atoms are evolved and absorbed at the crack tip. The diffused hydrogen then promotes dislocation emission and increases the dislocation density at theα’ phase boundaries and in the α’ phase. The crack initiation and propagation are results of the accumulation of highly hydrogen. At the same time, hydrogen enhances mobility of dislocations, then the crack propagates at a lower stress level.
关键词	电子束焊接钛合金应力腐蚀显微组织断口形貌
收录类别	CSCD
语种	中文
CSCD记录号	CSCD:6658733
引用统计	被引频次：10[CSCD] [CSCD记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/154971
专题	中国科学院金属研究所
作者单位	1.广东省焊接技术研究所(广东省中乌研究院广东省现代焊接技术重点实验室 2.中国科学院金属研究所
推荐引用方式 GB/T 7714	房卫萍,肖铁,张宇鹏,等. 超厚板TC4钛合金电子束焊接接头应力腐蚀敏感性[J]. 焊接学报,2019,40.0(012):121-128.
APA	房卫萍,肖铁,张宇鹏,徐望辉,&易耀勇.(2019).超厚板TC4钛合金电子束焊接接头应力腐蚀敏感性.焊接学报,40.0(012),121-128.
MLA	房卫萍,et al."超厚板TC4钛合金电子束焊接接头应力腐蚀敏感性".焊接学报 40.0.012(2019):121-128.