| XPS Analysis of Beads Formed by Fuse Breaking of Electric Copper Wire | |
| 其他题名 | XPS Analysis of Beads Formed by Fuse Breaking of Electric Copper Wire |
| Wu Ying; Meng Qingshan; Wang Xinming; Gao Wei; Di Man | |
| 2010 | |
| 发表期刊 | SPECTROSCOPY AND SPECTRAL ANALYSIS
 |
| ISSN | 1000-0593 |
| 卷号 | 30期号:5页码:1408-1412 |
| 摘要 | The in-depth composition of beads formed by fuse breaking of the electric copper wire in different circumstances was studied by XPS with Ar+ ion sputtering. In addition, the measured Auger spectra and the calculated Auger parameters were compared for differentiation of the substances of Cu and Cu2O. Corresponding to the sputtering depth, the molten product on a bead induced directly by fuse breaking of the copper wire without cover may be distinguished as three portions: surface layer with a drastic decrease in carbon content; intermediate layer with a gentle change in oxygen content and gradually diminished carbon peak, and consisting of Cu2O; transition layer without Cu2O and with a rapid decrease in oxygen content. While the molten product on a bead formed by fuse breaking of the copper wire after its insulating cover had been burned out may be distinguished as two portions: surface layer with carbon content decreasing quickly; subsurface layer without Cu2O and with carbon and oxygen content decreasing gradually. Thus, it can be seen that there was an obvious interface between the layered surface product and the substrate for the first type of bead, while as to the second type of bead there was no interface. As a result, the presence of Cu2O and the quantitative results can be used to identify the molten product on a bead induced directly by fuse breaking of the copper wire without cover and the molten product on a bead formed by fuse breaking of the cupper wire after its insulating cover had been burned out, as a complementary technique for the judgments of fire cause. |
| 关键词 | PERFORMANCE ZINC Depth etching X-ray photoelectron spectroscopy(XPS) Auger parameter Electrical short circuit molten mark |
| 收录类别 | CSCD |
| 语种 | 英语 |
| CSCD记录号 | CSCD:3913758 |
| 引用统计 | |
| 文献类型 | 期刊论文 |
| 条目标识符 | http://ir.imr.ac.cn/handle/321006/155131 |
| 专题 | 中国科学院金属研究所 |
| 作者单位 | 中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Wu Ying,Meng Qingshan,Wang Xinming,et al. XPS Analysis of Beads Formed by Fuse Breaking of Electric Copper Wire[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS,2010,30(5):1408-1412. |
| APA | Wu Ying,Meng Qingshan,Wang Xinming,Gao Wei,&Di Man.(2010).XPS Analysis of Beads Formed by Fuse Breaking of Electric Copper Wire.SPECTROSCOPY AND SPECTRAL ANALYSIS,30(5),1408-1412. |
| MLA | Wu Ying,et al."XPS Analysis of Beads Formed by Fuse Breaking of Electric Copper Wire".SPECTROSCOPY AND SPECTRAL ANALYSIS 30.5(2010):1408-1412. |
| 条目包含的文件 | 条目无相关文件。 | |||||
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论