Thermal shock and sulfuric acid corrosion behavior of enamel-nano-Ni composite/enamel-nano-nickel composite coating
Chen, Ken; Chen, Minghui; Yi, Aihua; Li, Kang; Zhu, Wen; Liao, Zhongmiao; Zhu, Shenglong; Wang, Fuhui
2020-10-01
Source PublicationINTERNATIONAL JOURNAL OF APPLIED GLASS SCIENCE
Volume11Issue:4Pages:784-795
AbstractDense and well-adherent enamel-nano-Ni composite/enamel-nano-nickel composite coatings were prepared on 304 steel. Their thermal shock (TS) resistance at 400 degrees C as well as the chemical stability in sulfuric acid solution were investigated, and compared with pure enamel coatings. Results indicated that the nanocomposite coatings with 5 wt% of Ni particles exhibited the best resistance to TS. Almost no spalling of the coating occurs after 50 cycles of TS at 400 degrees C. They also provided enough protective effect to the substrates from sulfuric acid corrosion. After 7 days of corrosion, the weight loss of Ni-5 enamel coating was only 1.107 mg/cm(.)(2)
DOI10.1111/ijag.15513
WOS IDWOS:000530521500001
Citation statistics
Cited Times:4[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/155702
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
Chen, Ken,Chen, Minghui,Yi, Aihua,et al. Thermal shock and sulfuric acid corrosion behavior of enamel-nano-Ni composite/enamel-nano-nickel composite coating[J]. INTERNATIONAL JOURNAL OF APPLIED GLASS SCIENCE,2020,11(4):784-795.
APA Chen, Ken.,Chen, Minghui.,Yi, Aihua.,Li, Kang.,Zhu, Wen.,...&Wang, Fuhui.(2020).Thermal shock and sulfuric acid corrosion behavior of enamel-nano-Ni composite/enamel-nano-nickel composite coating.INTERNATIONAL JOURNAL OF APPLIED GLASS SCIENCE,11(4),784-795.
MLA Chen, Ken,et al."Thermal shock and sulfuric acid corrosion behavior of enamel-nano-Ni composite/enamel-nano-nickel composite coating".INTERNATIONAL JOURNAL OF APPLIED GLASS SCIENCE 11.4(2020):784-795.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Chen, Ken]'s Articles
[Chen, Minghui]'s Articles
[Yi, Aihua]'s Articles
Baidu academic
Similar articles in Baidu academic
[Chen, Ken]'s Articles
[Chen, Minghui]'s Articles
[Yi, Aihua]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Chen, Ken]'s Articles
[Chen, Minghui]'s Articles
[Yi, Aihua]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.