La0.6Nd0．4Ni4．8Mn0．2M0．1（M=Cu，Zr）合金的贮氢性能研究

IMR OpenIR

	La0.6Nd0．4Ni4．8Mn0．2M0．1（M=Cu，Zr）合金的贮氢性能研究
其他题名	Study on Hydrogen Storage Properties of La0.6Nd0.4Ni4.8Mn0.2M0.1（M=Cu,Zr） Alloys
	李慎兰; 程宏辉; 邓小霞; 吕曼祺; 陈德敏; 杨柯
	2008
发表期刊	稀有金属材料与工程
ISSN	1002-185X
卷号	37.0 期号:004 页码:599-603
摘要	系统研究了非化学计量比合金La0.6Nd0．4Ni4．8Mn0．2M0．1（M=Cu，Zr）的贮氢性能。结果表明，添加Cu能提高合金的平台压力，减轻滞后效应；而添加Zr能够有效提高合金的动力学性能和抗粉化性能，降低平台压力。但Cu和Zr的添加使贮氢容量有所降低。研究表明，XRD（111）主峰半高宽FWHM值及晶格常数a／c值与合金的滞后因子有相同的变化趋势，平台压力、吸氢焓变与晶胞参数α有很好的线性关系。
其他摘要	Hydrogen storage properties of the nonstoichiometric alloys of La0.6Nd0.4Ni4.8Mn0.2M0.1（M=Cu,Zr） have been systematically investigated. Experimental results showed that Cu addition increased the plateau pressure and alleviated the hysteresis while Zr addition effectively improved the absorption kinetics, enhanced the pulverization resistant capability and lowered the plateau pressure. However, additions of Cu and Zr addition impaired the hydrogen storage capacity of the alloys. It was found that the hysteresis factors was correlated with FWHM of （111） peak and α/c value of the alloys, and both the plateau pressure and enthalpy had good linear relations With the lattice parameter α.
关键词	贮氢合金非化学计量比压力成分等温线动力学抗粉化性能
收录类别	CSCD
语种	中文
CSCD记录号	CSCD:3273272
引用统计	被引频次：1[CSCD] [CSCD记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/157766
专题	中国科学院金属研究所
作者单位	中国科学院金属研究所
推荐引用方式 GB/T 7714	李慎兰,程宏辉,邓小霞,等. La0.6Nd0．4Ni4．8Mn0．2M0．1（M=Cu，Zr）合金的贮氢性能研究[J]. 稀有金属材料与工程,2008,37.0(004):599-603.
APA	李慎兰,程宏辉,邓小霞,吕曼祺,陈德敏,&杨柯.(2008).La0.6Nd0．4Ni4．8Mn0．2M0．1（M=Cu，Zr）合金的贮氢性能研究.稀有金属材料与工程,37.0(004),599-603.
MLA	李慎兰,et al."La0.6Nd0．4Ni4．8Mn0．2M0．1（M=Cu，Zr）合金的贮氢性能研究".稀有金属材料与工程 37.0.004(2008):599-603.