Oxidation behavior of a nanocrystalline coating with low Ta content at high temperature

doi:10.1016/j.corsci.2020.109182

IMR OpenIR

	Oxidation behavior of a nanocrystalline coating with low Ta content at high temperature
	Yang, Lanlan 1; Wang, Jinlong 2,3; Yang, Ruize 1; Yang, Shasha 4; Jia, Yixuan 4; Chen, Minghui 2,3; Qiao, Yanxin 1; Guo, Pingyi 1; Zhu, Shenglong 2; Wang, Fuhui 3,4
通讯作者	Wang, Jinlong(wangjinlong@mail.neu.edu.cn) ; Chen, Minghui(mhchen@mail.neu.edu.cn)
	2021-03-01
发表期刊	CORROSION SCIENCE
ISSN	0010-938X
卷号	180 页码:11
摘要	Oxidation behavior of the nanocrystalline coating with low content of Ta on the N5 single-crystal superalloy is investigated at 1050 and 1150 degrees C. Results indicate that when the content of Ta in the nanocrystalline coating is reduced to 3 wt%, no gamma'-Ni-3(Al, Ta) will not be precipitated during oxidation. Then the activity of Ta is low, it will not be oxidized, which can be stable in the coating after oxidation. Therefore, the oxidation resistance of the nanocrystalline coating with low content of Ta in significantly improved.
关键词	Superalloys Metal coatings Oxidation
资助者	National Natural Science Foundation of China
DOI	10.1016/j.corsci.2020.109182
收录类别	SCI
语种	英语
资助项目	National Natural Science Foundation of China[51671053] ; National Natural Science Foundation of China[51471177] ; National Natural Science Foundation of China[52001142]
WOS研究方向	Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000609497900001
出版者	PERGAMON-ELSEVIER SCIENCE LTD
引用统计	被引频次：28[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/159045
专题	中国科学院金属研究所
通讯作者	Wang, Jinlong; Chen, Minghui
作者单位	1.Jiangsu Univ Sci & Technol, Sch Mat Sci & Engn, Zhenjiang 212003, Jiangsu, Peoples R China 2.Northeastern Univ, Shenyang Natl Lab Mat Sci, Shenyang 110819, Peoples R China 3.Northeastern Univ, Sch Mat Sci & Engn, Shenyang 110819, Peoples R China 4.Chinese Acad Sci, Inst Met Res, Lab Corros & Protect, Shenyang 110016, Peoples R China
推荐引用方式 GB/T 7714	Yang, Lanlan,Wang, Jinlong,Yang, Ruize,et al. Oxidation behavior of a nanocrystalline coating with low Ta content at high temperature[J]. CORROSION SCIENCE,2021,180:11.
APA	Yang, Lanlan.,Wang, Jinlong.,Yang, Ruize.,Yang, Shasha.,Jia, Yixuan.,...&Wang, Fuhui.(2021).Oxidation behavior of a nanocrystalline coating with low Ta content at high temperature.CORROSION SCIENCE,180,11.
MLA	Yang, Lanlan,et al."Oxidation behavior of a nanocrystalline coating with low Ta content at high temperature".CORROSION SCIENCE 180(2021):11.