| High Temperature Oxidation and Tribological Behaviors of NiCrAl-Graphite Self-Lubricating Composites | |
| Kong, Xuan1; Liu, Yang2; Chen, Minghui1; Zhang, Tao1; Wang, Fuhui1 | |
| Corresponding Author | Liu, Yang(liuyang@imr.ac.cn) ; Chen, Minghui(mhchen@mail.neu.edu.cn) |
| 2021-02-09 | |
| Source Publication | ACTA METALLURGICA SINICA-ENGLISH LETTERS
 |
| ISSN | 1006-7191 |
| Pages | 13 |
| Abstract | Nickel-graphite self-lubricating composites are a promising candidate to be used in turbine constructions that are usually exposed to high temperature oxidation and wear. However, the high-temperature stability of graphite as well as the effect that the oxide scale will play on the following wear process are still yet in debate. In this work, oxidation behavior of a NiCrAl-graphite composite and the subsequent friction and wear performances were studied. Results indicate that graphite is stable in the composites after oxidation at T <= 400 degrees C for 300 h, which contributes synergistically with the thin oxide film to self-lubrication. The friction coefficient is below 0.20 and the wear rate is similar to 1.43 x 10(-5) mm(3) N-1 m(-1). The composite has the highest friction coefficient and wear rate when it was suffered from the high temperature oxidation at 500 degrees C. Once it was oxidized at 600 degrees C, a glaze layer would develop during the subsequent sliding. It plays a positive role in improving tribological properties though in the absence of lubricant phase of graphite, with to be exactly the friction coefficient and wear rate reduced by 13% and 21%, respectively, in comparison with the case of oxidation at 500 degrees C. |
| Keyword | Oxidation Self-lubricating composites Wear Graphite |
| Funding Organization | Fundamental Research Funds for the Central Universities ; Ministry of Industry and Information Technology Project |
| DOI | 10.1007/s40195-020-01188-9 |
| Indexed By | SCI |
| Language | 英语 |
| Funding Project | Fundamental Research Funds for the Central Universities[N180212008] ; Fundamental Research Funds for the Central Universities[N181003001] ; Ministry of Industry and Information Technology Project[MJ-2017-J-99] |
| WOS Research Area | Metallurgy & Metallurgical Engineering |
| WOS Subject | Metallurgy & Metallurgical Engineering |
| WOS ID | WOS:000616448400001 |
| Publisher | CHINESE ACAD SCIENCES, INST METAL RESEARCH |
| Citation statistics | |
| Document Type | 期刊论文 |
| Identifier | http://ir.imr.ac.cn/handle/321006/160591 |
| Collection | 中国科学院金属研究所 |
| Corresponding Author | Liu, Yang; Chen, Minghui |
| Affiliation | 1.Northeastern Univ, Shenyang Natl Lab Mat Sci, Shenyang 110819, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China |
| Recommended Citation GB/T 7714 | Kong, Xuan,Liu, Yang,Chen, Minghui,et al. High Temperature Oxidation and Tribological Behaviors of NiCrAl-Graphite Self-Lubricating Composites[J]. ACTA METALLURGICA SINICA-ENGLISH LETTERS,2021:13. |
| APA | Kong, Xuan,Liu, Yang,Chen, Minghui,Zhang, Tao,&Wang, Fuhui.(2021).High Temperature Oxidation and Tribological Behaviors of NiCrAl-Graphite Self-Lubricating Composites.ACTA METALLURGICA SINICA-ENGLISH LETTERS,13. |
| MLA | Kong, Xuan,et al."High Temperature Oxidation and Tribological Behaviors of NiCrAl-Graphite Self-Lubricating Composites".ACTA METALLURGICA SINICA-ENGLISH LETTERS (2021):13. |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment