A synergy of different corrosion failure modes pertaining to T91 steel impacted by extreme lead-bismuth eutectic flow pattern

doi:10.1016/j.corsci.2020.109214

IMR OpenIR

	A synergy of different corrosion failure modes pertaining to T91 steel impacted by extreme lead-bismuth eutectic flow pattern
	Li, Cong 1,2; Fang, Xiaodong 1,3; Wang, Qingsheng 1; Shen, Mingli 4; Wang, Haoliang 5; Zeng, Xian 6; Liu, Yujing 7; Meng, Gang 1
通讯作者	Fang, Xiaodong(xdfang@aiofm.ac.cn) ; Wang, Qingsheng(qswang@aiofm.ac.cn) ; Shen, Mingli(mlshen@imr.ac.cn)
	2021-03-01
发表期刊	CORROSION SCIENCE
ISSN	0010-938X
卷号	180 页码:17
摘要	This paper reports an attempt to speculate about corrosion resistance of T91 steel to extreme lead-bismuth eutectic (LBE) flow pattern. We build a modified dynamic corrosion apparatus permitting assemblages of oxidation, erosion or dissolution attack proceeding together within oxygen-saturated LBE. After corrosion test at 400 degrees C up to 1000 h, discrepancies of corrosion performance under various flow patterns were described by diffusion or mass transfer kinetics as well as erosion mechanics. In justification of dense Fe-O layer and cracks across oxide scales detected within typical erosion cavities, we put forward oxide growth stress enhanced by high surface curvature.
关键词	T91 Oxygen-saturated LBE Oxidation Erosion Impact angle Cottrell atmosphere
资助者	Natural Science Foundation of Top Talent of SZTU ; CAS (Chinese Academy of Sciences) Pioneer Hundred Talents Program ; National Natural Science Foundation of China ; CAS-JSPS Joint Research Projects
DOI	10.1016/j.corsci.2020.109214
收录类别	SCI
语种	英语
资助项目	Natural Science Foundation of Top Talent of SZTU[2020101] ; CAS (Chinese Academy of Sciences) Pioneer Hundred Talents Program ; National Natural Science Foundation of China[11674324] ; National Natural Science Foundation of China[51803200] ; CAS-JSPS Joint Research Projects[GJHZ1891]
WOS研究方向	Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000612032300002
出版者	PERGAMON-ELSEVIER SCIENCE LTD
引用统计	被引频次：20[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/160980
专题	中国科学院金属研究所
通讯作者	Fang, Xiaodong; Wang, Qingsheng; Shen, Mingli
作者单位	1.Chinese Acad Sci, Anhui Inst Opt & Fine Mech, Hefei 230031, Peoples R China 2.Univ Sci & Technol China, Hefei 230026, Peoples R China 3.Shenzhen Technol Univ, Coll New Mat & New Energies, Shenzhen 518118, Guangdong, Peoples R China 4.Chinese Acad Sci, Shi Changxu Innovat Ctr Adv Mat, Inst Met Res, Wencui Rd 62, Shenyang 110016, Peoples R China 5.Dongguan Univ Technol, Sch Mech Engn, Dongguan 523808, Peoples R China 6.China Nucl Power Technol Res Inst, Sci & Technol Bldg,1001 Shangbuzhong Rd, Shenzhen 518031, Peoples R China 7.Changsha Univ Sci & Technol, Coll Mat Sci & Engn, 960 2nd Sect,Wanjiali RD S, Changsha 410004, Hunan, Peoples R China
推荐引用方式 GB/T 7714	Li, Cong,Fang, Xiaodong,Wang, Qingsheng,et al. A synergy of different corrosion failure modes pertaining to T91 steel impacted by extreme lead-bismuth eutectic flow pattern[J]. CORROSION SCIENCE,2021,180:17.
APA	Li, Cong.,Fang, Xiaodong.,Wang, Qingsheng.,Shen, Mingli.,Wang, Haoliang.,...&Meng, Gang.(2021).A synergy of different corrosion failure modes pertaining to T91 steel impacted by extreme lead-bismuth eutectic flow pattern.CORROSION SCIENCE,180,17.
MLA	Li, Cong,et al."A synergy of different corrosion failure modes pertaining to T91 steel impacted by extreme lead-bismuth eutectic flow pattern".CORROSION SCIENCE 180(2021):17.