Effect of Heat Treatment on Microstructure and Tensile Property of Ti-6Al-6V-2Sn Alloy

doi:10.3390/met11040556

IMR OpenIR

	Effect of Heat Treatment on Microstructure and Tensile Property of Ti-6Al-6V-2Sn Alloy
	Wang, Qirui 1,2; Lei, Xiaofei 2; Hu, Ming 2; Xu, Xin 3; Yang, Rui 2; Dong, Limin 2
通讯作者	Xu, Xin(xuxin58@mail.sysu.edu.cn) ; Dong, Limin(lmdong@imr.ac.cn)
	2021-04-01
发表期刊	METALS
卷号	11 期号:4 页码:12
摘要	The microstructure and tensile properties of Ti-6Al-6V-2Sn alloy heat-treated at different solution and aging temperatures has been systematically investigated. Specimens were solution-treated at 970 degrees C (above the beta transus) and 920 degrees C (below the beta transus), respectively, followed by water quenching. When the alloy is quenched from 970 degrees C, alpha' (hcp) and alpha '' (orthorhombic) martensite phases co-exist in the microstructure. When it is quenched from 920 degrees C, alpha ' martensite phase does not form, while equiaxial primary alpha (alpha(p)) phase and alpha '' are found in the microstructure. The results also show that the strength of the alloy increases but the ductility deteriorates as the solution temperature becomes higher when the aging treatment is unchanged. This is because the volume fraction of equiaxial alpha(p) phase is lower but the volume fraction of the acicular secondary alpha (alpha(s)) phase is higher for higher solution temperature. When the alloy is aged at different temperatures after the solution treatment at 900 degrees C, the strength of the alloy decreases with the increase of aging temperature and the ductility shows the opposite trend as the size of the acicular alpha(s) becomes longer and its volume fraction is lower at higher aging temperature.
关键词	Ti-6Al-6V-2Sn titanium alloy heat treatment microstructure
资助者	National Science Foundation for Young Scientists of China
DOI	10.3390/met11040556
收录类别	SCI
语种	英语
资助项目	National Science Foundation for Young Scientists of China[51801199]
WOS研究方向	Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000643274300001
出版者	MDPI
引用统计	被引频次：9[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/162061
专题	中国科学院金属研究所
通讯作者	Xu, Xin; Dong, Limin
作者单位	1.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China 2.Chinese Acad Sci, Shi Changxu Innovat Ctr Adv Mat, Inst Met Res, Shenyang 110016, Peoples R China 3.Sun Yat Sen Univ, Sch Mat, Shenzhen 518107, Peoples R China
推荐引用方式 GB/T 7714	Wang, Qirui,Lei, Xiaofei,Hu, Ming,et al. Effect of Heat Treatment on Microstructure and Tensile Property of Ti-6Al-6V-2Sn Alloy[J]. METALS,2021,11(4):12.
APA	Wang, Qirui,Lei, Xiaofei,Hu, Ming,Xu, Xin,Yang, Rui,&Dong, Limin.(2021).Effect of Heat Treatment on Microstructure and Tensile Property of Ti-6Al-6V-2Sn Alloy.METALS,11(4),12.
MLA	Wang, Qirui,et al."Effect of Heat Treatment on Microstructure and Tensile Property of Ti-6Al-6V-2Sn Alloy".METALS 11.4(2021):12.