Microstructure and Properties of 2Cr13-xMo Stainless Steels Fabricated by Direct Laser Deposition

doi:10.1007/s12540-021-01035-1

IMR OpenIR

	Microstructure and Properties of 2Cr13-xMo Stainless Steels Fabricated by Direct Laser Deposition
	Liang, Jing 1; Lin, Ziyang 1; Yin, Xiuyuan 1; Chen, Suiyuan 1; Liu, Changsheng 1; Chai, Ruihong 1; Zhang, Hongwei 2; Tang, Guangquan 2; Tian, Kun 3
通讯作者	Liang, Jing(liangj@atm.neu.edu.cn)
	2021-09-09
发表期刊	METALS AND MATERIALS INTERNATIONAL
ISSN	1598-9623
页码	11
摘要	In this paper, 2Cr13 stainless steels with different Mo contents (x = 0 wt%, 0.5 wt%, 1.0 wt%, 1.5 wt%, 2.0 wt%) were fabricated by Direct Laser Deposition (DLD) technology. The effects of Mo element on the microstructure evolution and comprehensive properties such as corrosion resistance and wear resistance of 2Cr13 stainless steel were investigated in detail. The results showed that the microstructure for the DLD 2Cr13 stainless steel was mainly composed of martensite, ferrite, and a small amount of -Mo2C and -Cr23C6 carbides. With the content of Mo increased from 0.5 to 1.5 wt%, the martensitic microstructure was refined and more dispersed -Mo2C and -Cr23C6 carbides were formed. The average microhardness and corrosion resistance of the DLD 2Cr(13-x)Mo were increased with the Mo content increased from 0 to 1.0 wt%, and then decreased when the Mo content exceeded 1.0 wt%. For the DLD 2Cr13-1.0 wt% Mo, the average microhardness reached up to 620 -HV0.2, and the highest corrosion resistance (self-corrosion potential - 0.34 V) was obtained, in which the selfcorrosion potential was 0.05 higher than that of DLD 2Cr13 stainless steel. The wear resistance of the DLD 2Cr13-xMo gradually increased with the increase of the Mo, the wear mass loss of DLD 2Cr(13-x)Mo (x = 1.0 wt%) was only 37% that of DLD 2Cr(13) stainless steel.
关键词	Direct laser deposition (DLD) 2Cr13 stainless steel Mo addition Corrosion resistance Microstructure
资助者	National Key R&D Program of China ; Joint Founds of NSFC-Liaoning ; Founds of Green Manufacturing System Integration Project of the Industry and Information Ministry of China (2017) ; Key R&D Projects in Liaoning Province
DOI	10.1007/s12540-021-01035-1
收录类别	SCI
语种	英语
资助项目	National Key R&D Program of China[2016YFB1100203] ; Joint Founds of NSFC-Liaoning[U1508213] ; Founds of Green Manufacturing System Integration Project of the Industry and Information Ministry of China (2017) ; Key R&D Projects in Liaoning Province[2020JH2/10100022]
WOS研究方向	Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000694615900001
出版者	KOREAN INST METALS MATERIALS
引用统计	被引频次：6[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/166904
专题	中国科学院金属研究所
通讯作者	Liang, Jing
作者单位	1.Northeastern Univ, Sch Mat Sci & Engn, Key Lab Anisotropy & Texture Mat, Key Lab Addit Mfg & Remfg Mat,Minist Educ, Shenyang 110819, Liaoning, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 3.Shenyang Ruixian Intelligent Equipment Technol Co, Shenyang, Peoples R China
推荐引用方式 GB/T 7714	Liang, Jing,Lin, Ziyang,Yin, Xiuyuan,et al. Microstructure and Properties of 2Cr13-xMo Stainless Steels Fabricated by Direct Laser Deposition[J]. METALS AND MATERIALS INTERNATIONAL,2021:11.
APA	Liang, Jing.,Lin, Ziyang.,Yin, Xiuyuan.,Chen, Suiyuan.,Liu, Changsheng.,...&Tian, Kun.(2021).Microstructure and Properties of 2Cr13-xMo Stainless Steels Fabricated by Direct Laser Deposition.METALS AND MATERIALS INTERNATIONAL,11.
MLA	Liang, Jing,et al."Microstructure and Properties of 2Cr13-xMo Stainless Steels Fabricated by Direct Laser Deposition".METALS AND MATERIALS INTERNATIONAL (2021):11.