Damage behavior and mechanism of SiCp/Al composites under biaxial tension

doi:10.1016/j.matchar.2021.111402

IMR OpenIR

	Damage behavior and mechanism of SiCp/Al composites under biaxial tension
	Yuan, Zhanwei 1,2; Shen, Qiuyan 1,2; Liu, Huan 1,2; Ma, Xinkai 3; Zhang, Xuemin 1; Fu, Qinqin 4,5; Wang, Quanzhao 6; Zhang, Laichang 7
通讯作者	Yuan, Zhanwei(yuanyekingfly@163.com) ; Wang, Quanzhao()
	2021-10-01
发表期刊	MATERIALS CHARACTERIZATION
ISSN	1044-5803
卷号	180 页码:12
摘要	The deformation behavior and damage mechanism of 17 vol% SiCp/Al composites under biaxial loading were studied by biaxial tension and nano-indentation tests. The results showed that in the process of biaxial tension, the composite in rolling normal direction has underwent less severe damage compared to that in the two tensile directions. However, interfacial debonding, particle shedding and microcrack propagation are accompanied in all three directions. The crack size becomes larger as the cracks gradually propagate on the surface of the material, leading to the failure of the composite. The micromechanical properties of the composite show a trend from a slow increase to a sharp increase. In addition, the distribution characteristics of stress, equivalent plastic strain and stress triaxiality of SiCp/Al composites under biaxial tensile stress are simulated by finite element method. The results showed that the stress and strain of composites increase rapidly along the diagonal direction. In the process of deformation, the stress triaxiality increases gradually, which makes the microcracks propagate easily, so the fracture surface of the composite presents a large number of dimples.
关键词	SiCp/Al composites Biaxial tensile test Nanoindentation Damage behavior Finite element method
资助者	China Postdoctoral Science Foundation ; Nature Science Foundation of Shaanxi ; Key Research and Development Plan in Shaanxi Province of China ; Fundamental Research Funds for the Central Universities, CHD ; Key Laboratory of Advanced Technologies of Materials, Ministry of Education China, Southwest Jiaotong University
DOI	10.1016/j.matchar.2021.111402
收录类别	SCI
语种	英语
资助项目	China Postdoctoral Science Foundation[2017M623084] ; Nature Science Foundation of Shaanxi[2021JQ-286] ; Key Research and Development Plan in Shaanxi Province of China[2021GY-211] ; Fundamental Research Funds for the Central Universities, CHD[300102311403] ; Key Laboratory of Advanced Technologies of Materials, Ministry of Education China, Southwest Jiaotong University[KLATM202007]
WOS研究方向	Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering ; Materials Science, Characterization & Testing
WOS记录号	WOS:000697476000007
出版者	ELSEVIER SCIENCE INC
引用统计	被引频次：6[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/167030
专题	中国科学院金属研究所
通讯作者	Yuan, Zhanwei; Wang, Quanzhao
作者单位	1.Changan Univ, Sch Mat Sci & Engn, Xian 710061, Shaanxi, Peoples R China 2.Changan Univ, Lab Adv Technol & Equipment, Xian 710061, Shaanxi, Peoples R China 3.Southwest Jiaotong Univ, Key Lab Adv Technol Mat, Minist Educ China, Chengdu 610031, Peoples R China 4.Xi An Jiao Tong Univ, Ctr Adv Mat Performance Nanoscale CAMP Nano, Xian 710049, Shaanxi, Peoples R China 5.Xi An Jiao Tong Univ, Hysitron Appl Res Ctr China HARCC, State Key Lab Mech Behav Mat, Xian 710049, Shaanxi, Peoples R China 6.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 7.Edith Cowan Univ, Sch Engn, 270 Joondalup Dr, Joondalup, WA 6027, Australia
推荐引用方式 GB/T 7714	Yuan, Zhanwei,Shen, Qiuyan,Liu, Huan,et al. Damage behavior and mechanism of SiCp/Al composites under biaxial tension[J]. MATERIALS CHARACTERIZATION,2021,180:12.
APA	Yuan, Zhanwei.,Shen, Qiuyan.,Liu, Huan.,Ma, Xinkai.,Zhang, Xuemin.,...&Zhang, Laichang.(2021).Damage behavior and mechanism of SiCp/Al composites under biaxial tension.MATERIALS CHARACTERIZATION,180,12.
MLA	Yuan, Zhanwei,et al."Damage behavior and mechanism of SiCp/Al composites under biaxial tension".MATERIALS CHARACTERIZATION 180(2021):12.