Corrosion Behavior of Zinc-Aluminum-Magnesium Coated Steel in Simulated Marine Atmosphere

doi:10.20964/2022.05.16

IMR OpenIR

	Corrosion Behavior of Zinc-Aluminum-Magnesium Coated Steel in Simulated Marine Atmosphere
	Gu, Tianzhen 1,2; Zhang, Peng 3,4; Guo, Mingxiao 1,2; Peng, Can 1,2; Ma, Cheng 4; Liu, Yuwei 1; Wang, Zhenyao 1
通讯作者	Liu, Yuwei(ywliu12s@imr.ac.cn) ; Wang, Zhenyao(zhywang@imr.ac.cn)
	2022-05-01
发表期刊	INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE
ISSN	1452-3981
卷号	17 期号:5 页码:14
摘要	The corrosion behavior of zinc -aluminum -magnesium (ZAM) coated steel in a simulated marine atmosphere was investigated using compositional, morphological, electrochemical, and mass loss analyses. The results revealed that the corrosion rate of ZAM coated steel fluctuated because of the corrosion products formed during its exposure to the marine atmosphere, and the mass loss after 1848 h of exposure was 27.37 g.m(-2) after 1848 hours' exposure. The corrosion preferentially occurred in the eutectic phases, especially in the eutectic phases near the primary zinc phase and with an area smaller than the primary zinc phase. As the exposure time increased, some of the corrosion products flaked off from the coating, leading to the aggravation of local corrosion and the formation of corrosion pits. Moreover, the corrosion products in the corrosion pits were dissolved, which can be attributed to the decrease in pH caused by the consumption of hydroxides during the chemical reactions of the corrosion process.
关键词	ZAM coated steel atmospheric corrosion mass loss electrochemical measurements corrosion pits
资助者	Liaoning Shenyang Soil and Atmosphere Corrosion of Material National Observation and Research Station
DOI	10.20964/2022.05.16
收录类别	SCI
语种	英语
资助项目	Liaoning Shenyang Soil and Atmosphere Corrosion of Material National Observation and Research Station
WOS研究方向	Electrochemistry
WOS类目	Electrochemistry
WOS记录号	WOS:000798898500021
出版者	ESG
引用统计	被引频次：4[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/174111
专题	中国科学院金属研究所
通讯作者	Liu, Yuwei; Wang, Zhenyao
作者单位	1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China 3.China Iron & Steel Res Inst Grp, Natl Engn Lab Adv Coating Technol Mat, Beijing 100081, Peoples R China 4.HBIS Grp Technol Res Inst, Shijiazhuang 050023, Hebei, Peoples R China
推荐引用方式 GB/T 7714	Gu, Tianzhen,Zhang, Peng,Guo, Mingxiao,et al. Corrosion Behavior of Zinc-Aluminum-Magnesium Coated Steel in Simulated Marine Atmosphere[J]. INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE,2022,17(5):14.
APA	Gu, Tianzhen.,Zhang, Peng.,Guo, Mingxiao.,Peng, Can.,Ma, Cheng.,...&Wang, Zhenyao.(2022).Corrosion Behavior of Zinc-Aluminum-Magnesium Coated Steel in Simulated Marine Atmosphere.INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE,17(5),14.
MLA	Gu, Tianzhen,et al."Corrosion Behavior of Zinc-Aluminum-Magnesium Coated Steel in Simulated Marine Atmosphere".INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE 17.5(2022):14.