Ultrafine grained metastable Ti6Al4V5Cu alloy with high strength and excellent low-cycle fatigue property
Song, Wei1,2; Wang, Hai1; Li, Yi1,2; Zhang, Shuyuan1; Ren, Ling1; Yang, Ke1
通讯作者Ren, Ling(lren@imr.ac.cn)
2022-12-01
发表期刊JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
ISSN1005-0302
卷号129页码:240-250
摘要The insufficient low-cycle fatigue properties of titanium alloys under cyclic heavy loading are regarded as a challenge for their security in service. In recent years, a large number of studies have found that the transformation induced plasticity (TRIP) effect could hinder the propagation of fatigue cracks, which significantly improved the low-cycle fatigue properties of titanium alloys. However, the coarse beta-phase grains and the soft phase transformation product a alpha '' phase in TRIP titanium alloys impair their tensile strength, which restrict their applications in engineering. To this end, a Ti6Al4V5Cu alloy with TRIP effect was developed in this work. It was proposed to use the mutual restraint between the alpha and beta-phases in the material to refine the grains, and through composition optimization, the phase transformation product would be the alpha' phase, which has a higher strength than the a alpha '' phase. Thus, the strength of the Ti6Al4V5Cu alloy can be improved. The results showed that the tensile strength and elongation of the TRIP Ti6Al4V5Cu alloy was 1286 MPa and 22%, which was 23.7% and 46.7% higher than that of the traditional Ti6Al4V alloy, respectively. Besides, under the same strain amplitude, the fatigue life of the Ti6Al4V5Cu alloy was 2-5 times longer than that of the Ti6Al4V alloy. Furthermore, we clarified the mechanisms of improving the tensile strength and fatigue properties of the Ti6Al4V5Cu alloy, which would lay a research foundation for the development of high-performance titanium alloys. (C) 2022 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.
关键词Transformation induced plasticity Ti alloys Low-cycle fatigue Work hardening Crack propagation
资助者National Key Research and Development Program of China ; Natural Science Foundation of China ; Liaoning Revitalization Talents Program ; Doctoral Scientific Research Foundation of Liaoning Province ; Binzhou Weiqiao Guoke Institute of Advanced Technology
DOI10.1016/j.jmst.2022.05.007
收录类别SCI
语种英语
资助项目National Key Research and Development Program of China[2018YFC1106600] ; Natural Science Foundation of China[51631009] ; Liaoning Revitalization Talents Program[XLYC1807069] ; Doctoral Scientific Research Foundation of Liaoning Province[2020BS002] ; Binzhou Weiqiao Guoke Institute of Advanced Technology
WOS研究方向Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS记录号WOS:000810926900009
出版者JOURNAL MATER SCI TECHNOL
引用统计
被引频次:11[WOS]   [WOS记录]     [WOS相关记录]
文献类型期刊论文
条目标识符http://ir.imr.ac.cn/handle/321006/174363
专题中国科学院金属研究所
通讯作者Ren, Ling
作者单位1.Chinese Acad Sci, Inst Met Res, Shi Changxu Innovat Ctr Adv Mat, Shenyang 110016, Peoples R China
2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China
推荐引用方式
GB/T 7714
Song, Wei,Wang, Hai,Li, Yi,et al. Ultrafine grained metastable Ti6Al4V5Cu alloy with high strength and excellent low-cycle fatigue property[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2022,129:240-250.
APA Song, Wei,Wang, Hai,Li, Yi,Zhang, Shuyuan,Ren, Ling,&Yang, Ke.(2022).Ultrafine grained metastable Ti6Al4V5Cu alloy with high strength and excellent low-cycle fatigue property.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,129,240-250.
MLA Song, Wei,et al."Ultrafine grained metastable Ti6Al4V5Cu alloy with high strength and excellent low-cycle fatigue property".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 129(2022):240-250.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Song, Wei]的文章
[Wang, Hai]的文章
[Li, Yi]的文章
百度学术
百度学术中相似的文章
[Song, Wei]的文章
[Wang, Hai]的文章
[Li, Yi]的文章
必应学术
必应学术中相似的文章
[Song, Wei]的文章
[Wang, Hai]的文章
[Li, Yi]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。