| The effect of NaCl-induced corrosion on Ti60′s hot salt stress corrosion cracking | |
| Chen, Wenzheng1; Wang, Wenquan1; Liu, Li1; Liu, Rui1; Cui, Yu2; Chen, Zhiyong2; Wang, Qingjiang2; Wang, Fuhui1 | |
| Corresponding Author | Liu, Li(liuli@mail.neu.edu.cn) |
| 2024 | |
| Source Publication | CORROSION SCIENCE
 |
| ISSN | 0010-938X |
| Volume | 226Pages:17 |
| Abstract | The hot salt stress corrosion cracking (HSSCC) behaviour of Ti60 alloy at 600 degrees C in moist air has been studied, focusing on NaCl-induced corrosion as an embrittlement mechanism. NaCl-induced active corrosion was proven to happen at the crack front. This corrosion process promoted the loss of metal and the ingress of O, leading to quick O embrittlement of the alloy. In the alloy, the beta phase can somewhat inhibit HSSCC due to its less sensitivity to corrosion-promoted O ingress. Phase boundaries have strong corrosion sensitivity to NaCl-induced corrosion. Thus, phase boundaries are prone to cracking. |
| Keyword | Titanium Alloy Stress-corrosion cracking High temperature corrosion TEM |
| Funding Organization | National Natural Science Foundation of China |
| DOI | 10.1016/j.corsci.2023.111677 |
| Indexed By | SCI |
| Language | 英语 |
| Funding Project | National Natural Science Foundation of China[52301082] |
| WOS Research Area | Materials Science ; Metallurgy & Metallurgical Engineering |
| WOS Subject | Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
| WOS ID | WOS:001119262000001 |
| Publisher | PERGAMON-ELSEVIER SCIENCE LTD |
| Citation statistics | |
| Document Type | 期刊论文 |
| Identifier | http://ir.imr.ac.cn/handle/321006/177130 |
| Collection | 中国科学院金属研究所 |
| Corresponding Author | Liu, Li |
| Affiliation | 1.Northeastern Univ, Shenyang Natl Lab Mat Sci, Shenyang 110819, Peoples R China 2.Chinese Acad Sci, Shi Changxu Innovat Ctr Adv Mat, Inst Met Res, Wenhua Rd 72, Shenyang 110016, Peoples R China |
| Recommended Citation GB/T 7714 | Chen, Wenzheng,Wang, Wenquan,Liu, Li,et al. The effect of NaCl-induced corrosion on Ti60′s hot salt stress corrosion cracking[J]. CORROSION SCIENCE,2024,226:17. |
| APA | Chen, Wenzheng.,Wang, Wenquan.,Liu, Li.,Liu, Rui.,Cui, Yu.,...&Wang, Fuhui.(2024).The effect of NaCl-induced corrosion on Ti60′s hot salt stress corrosion cracking.CORROSION SCIENCE,226,17. |
| MLA | Chen, Wenzheng,et al."The effect of NaCl-induced corrosion on Ti60′s hot salt stress corrosion cracking".CORROSION SCIENCE 226(2024):17. |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment