| Synergistic effect of crevice corrosion and galvanic coupling on 304SS fasteners degradation in chloride environments | |
| Daniel, Enobong Felix1; Wang, Changgang1; Li, Chao1; Dong, Junhua1; Zhang, Dongjiu3; Zhong, Wenan3; Zhong, Sheng3; Udoh, Inime Ime4; Okafor, Peter Chukwuemeka5 | |
| 2023 | |
| Source Publication | NPJ MATERIALS DEGRADATION
 |
| ISSN | 2397-2106 |
| Volume | 7Issue:1 |
| Abstract | The synergistic effect of crevice corrosion and galvanic coupling on the degradation of 304 stainless steel fasteners exposed to a chloride environment was investigated using electrochemical and surface analysis techniques. Results obtained revealed that the crevice region of the fastener showed lower corrosion resistance due to decreased surface passivation induced by the crevice geometry and low oxygen conditions, while the exposed region with a higher oxygen supply exhibited improved corrosion resistance. Coupling of the exposed and crevice regions of the fastener demonstrated accelerated corrosion attributable to galvanic effect. The driving force for the galvanic effect on the fastener was linked to three (3) key factors: (I) the potential difference established between the different regions on the fastener surface due to uneven oxygen distribution, (II) the difference in the solution environment, and (III) the difference in surface properties (active-passive surface). Morphological studies showed localised corrosion occurring mainly in the crevice. |
| Language | 英语 |
| Document Type | 期刊论文 |
| Identifier | http://ir.imr.ac.cn/handle/321006/177289 |
| Collection | 中国科学院金属研究所 |
| Affiliation | 1.University of Science & Technology of China, CAS 2.Institute of Metal Research, CAS 3.Xichang Satellite Launch Ctr 4.Shenyang Ligong University 5.University of Calabar |
| Recommended Citation GB/T 7714 | Daniel, Enobong Felix,Wang, Changgang,Li, Chao,et al. Synergistic effect of crevice corrosion and galvanic coupling on 304SS fasteners degradation in chloride environments[J]. NPJ MATERIALS DEGRADATION,2023,7(1). |
| APA | Daniel, Enobong Felix.,Wang, Changgang.,Li, Chao.,Dong, Junhua.,Zhang, Dongjiu.,...&Okafor, Peter Chukwuemeka.(2023).Synergistic effect of crevice corrosion and galvanic coupling on 304SS fasteners degradation in chloride environments.NPJ MATERIALS DEGRADATION,7(1). |
| MLA | Daniel, Enobong Felix,et al."Synergistic effect of crevice corrosion and galvanic coupling on 304SS fasteners degradation in chloride environments".NPJ MATERIALS DEGRADATION 7.1(2023). |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment