Corrosion evolution of high-temperature formed oxide film on pure Sn solder substrate

doi:10.1016/S1003-6326(22)66073-4

IMR OpenIR

	Corrosion evolution of high-temperature formed oxide film on pure Sn solder substrate
	Zhao, Hui 1; Sun, Xu 1,2; Hao, Long 2,3; Wang, Jian-qiu 2,3; Yang, Jing-mei 4
通讯作者	Hao, Long(chinahaolong@126.com)
	2022-12-01
发表期刊	TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA
ISSN	1003-6326
卷号	32 期号:12 页码:3998-4013
摘要	The evolution of morphology, composition, thickness and corrosion resistance of the oxide film on pure Sn solder substrate submitted to high-temperature aging in 150 degrees C dry atmosphere was investigated. The results indicate that high-temperature aging accelerates the dehydration of Sn(OH)(4) in the pre-existing native oxide film to form SnO2 and facilitates the oxidation of fresh Sn substrate, resulting in the gradual increase in oxide film thickness and surface roughness with prolonging aging time. However, the corrosion resistance of the film initially is enhanced and then deteriorated with an extending aging time. Besides, the formation and evolution mechanisms of the oxide film with aging time were discussed.
关键词	pure Sn solder oxide film high-temperature aging corrosion resistance
资助者	CAS Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Sciences
DOI	10.1016/S1003-6326(22)66073-4
收录类别	SCI
语种	英语
资助项目	CAS Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Sciences
WOS研究方向	Metallurgy & Metallurgical Engineering
WOS类目	Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000988117800012
出版者	ELSEVIER
引用统计	被引频次：4[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/177977
专题	中国科学院金属研究所
通讯作者	Hao, Long
作者单位	1.Shenyang Ligong Univ, Sch Mat Sci & Engn, Shenyang 110159, Peoples R China 2.Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China 3.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Peoples R China 4.Shenyang Aircraft Ind Grp Corp Ltd, Shenyang 110034, Peoples R China
推荐引用方式 GB/T 7714	Zhao, Hui,Sun, Xu,Hao, Long,et al. Corrosion evolution of high-temperature formed oxide film on pure Sn solder substrate[J]. TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,2022,32(12):3998-4013.
APA	Zhao, Hui,Sun, Xu,Hao, Long,Wang, Jian-qiu,&Yang, Jing-mei.(2022).Corrosion evolution of high-temperature formed oxide film on pure Sn solder substrate.TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,32(12),3998-4013.
MLA	Zhao, Hui,et al."Corrosion evolution of high-temperature formed oxide film on pure Sn solder substrate".TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA 32.12(2022):3998-4013.