Preparation and Oxidation Behaviors of C/SiC-BN Composites

doi:10.15541/jim20230583

IMR OpenIR

	Preparation and Oxidation Behaviors of C/SiC-BN Composites
	Jiang Lingyi 1,2; Pang Shengyang 2; Yang Chao 1; Zhang Yue 1; Hu Chenglong 2; Tang Sufang 2
通讯作者	Tang Sufang(sftang@imr.ac.cn)
	2024-07-20
发表期刊	JOURNAL OF INORGANIC MATERIALS
ISSN	1000-324X
卷号	39 期号:7 页码:779-786
摘要	As thermal structural materials operating at high temperatures, C/SiC composites have extensive applications as thermal protection systems in aerospace vehicles. However, their limited antioxidant performance at low and medium temperatures restricts their utilization in diverse fields. In this work, an improved slurry impregnation technique was employed to introduce antioxidant component BN at different contents into the carbon fiber felts by adjusting the ceramic content in the slurry, and then densified the felts to prepare C/SiC-BN composites using reaction melt infiltration method. Effects of BN content on the composition, microstructure and oxidation behaviors of the composites were systematically studied, and relevant oxidation mechanisms were explored. Experimental results indicate that introduction of BN particles significantly reduces the open porosity of C/SiC and enhances the initial oxidation temperature of C/SiC. The C/SiC-BN composite with 3% BN (mass fraction, sample B3) has optimal antioxidant performance, and the corresponding mass loss rates in static air at 900, 1200 and 1500 degrees C for 1 h are 0.009%, -0.301%, and -0.596%, respectively. After oxidation at 1500 degrees C, the strength retention rate of sample B3 is up to 52%. At 900 degrees C, the mass change is dominated by slow weight loss controlled by O-2 diffusion and oxidation of C and BN. At 1200 degrees C, the oxidation rates of C and BN phases increase while SiC begins to undergo significant oxidation. New formed oxidation products, such as B2O3, borosilicate and SiO2, gradually slow the diffusion of O-2 and reduce the damage of carbon. At 1500 degrees C, the oxidation rate of SiC is accelerated obviously. Finally, a continuous oxidation film formed by generated SiO2 retards the inward diffusion of O-2, and overflow of gas products (such as B2O3 and CO) and continuous formation of SiO2 dominate the oxidation process.
关键词	slurry impregnation C/SiC BN microstructure oxidation behavior
资助者	National Natural Science Foundation of China
DOI	10.15541/jim20230583
收录类别	SCI
语种	英语
资助项目	National Natural Science Foundation of China[52272075] ; National Natural Science Foundation of China[U20A20242]
WOS研究方向	Materials Science
WOS类目	Materials Science, Ceramics
WOS记录号	WOS:001268954700005
出版者	SCIENCE PRESS
引用统计
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/189190
专题	中国科学院金属研究所
通讯作者	Tang Sufang
作者单位	1.Shenyang Univ Technol, Sch Mat Sci & Engn, Shenyang 110870, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China
推荐引用方式 GB/T 7714	Jiang Lingyi,Pang Shengyang,Yang Chao,et al. Preparation and Oxidation Behaviors of C/SiC-BN Composites[J]. JOURNAL OF INORGANIC MATERIALS,2024,39(7):779-786.
APA	Jiang Lingyi,Pang Shengyang,Yang Chao,Zhang Yue,Hu Chenglong,&Tang Sufang.(2024).Preparation and Oxidation Behaviors of C/SiC-BN Composites.JOURNAL OF INORGANIC MATERIALS,39(7),779-786.
MLA	Jiang Lingyi,et al."Preparation and Oxidation Behaviors of C/SiC-BN Composites".JOURNAL OF INORGANIC MATERIALS 39.7(2024):779-786.