Hydrogen Embrittlement Behavior of X42 Pipeline Steel in Gaseous Hydrogen with Different Pressures

doi:10.1007/s11665-024-10457-y

IMR OpenIR

	Hydrogen Embrittlement Behavior of X42 Pipeline Steel in Gaseous Hydrogen with Different Pressures
	Wang, Huyue 1,2; Ming, Hongliang 2; Wang, Jianqiu 2,3; Han, En-Hou 2,3
通讯作者	Ming, Hongliang(hlming12s@imr.ac.cn) ; Wang, Jianqiu(wangjianqiu@imr.ac.cn)
	2024-11-18
发表期刊	JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
ISSN	1059-9495
页码	10
摘要	This work explored the effect of pressure on the hydrogen embrittlement behavior of X42 pipeline steel by using tensile test. Fracture mode changes from ductile fracture when exposed to nitrogen to coexistence of ductile and brittle fracture in the presence of hydrogen. Furthermore, it has been observed that raising the hydrogen pressure can significantly increase the susceptibility to hydrogen embrittlement. This is supported by the presence of a greater proportion of brittle characteristic area on the cross section at fracture. The hydrogen embrittlement susceptibility index reaches 13.05% at pressure of 4 MPa, approximately 1.7 times higher than that at the pressure of 2 MPa.
关键词	failure analysis fractography gaseous hydrogen hydrogen embrittlement mechanical testing X42 pipeline steel
资助者	National Key R&D Program of China ; Youth Innovation Promotion Association CAS
DOI	10.1007/s11665-024-10457-y
收录类别	SCI
语种	英语
资助项目	National Key R&D Program of China[2021YFB4001601] ; Youth Innovation Promotion Association CAS[2022187]
WOS研究方向	Materials Science
WOS类目	Materials Science, Multidisciplinary
WOS记录号	WOS:001357758000001
出版者	SPRINGER
引用统计
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/191566
专题	中国科学院金属研究所
通讯作者	Ming, Hongliang; Wang, Jianqiu
作者单位	1.Northeastern Univ, Sch Mat Sci & Engn, Shenyang 110819, Peoples R China 2.Chinese Acad Sci, CAS Key Lab Nucl Mat & Safety Assessment, Inst Met Res, Shenyang 110016, Peoples R China 3.Inst Corros Sci & Technol, Guangzhou 510530, Guangdong, Peoples R China
推荐引用方式 GB/T 7714	Wang, Huyue,Ming, Hongliang,Wang, Jianqiu,et al. Hydrogen Embrittlement Behavior of X42 Pipeline Steel in Gaseous Hydrogen with Different Pressures[J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE,2024:10.
APA	Wang, Huyue,Ming, Hongliang,Wang, Jianqiu,&Han, En-Hou.(2024).Hydrogen Embrittlement Behavior of X42 Pipeline Steel in Gaseous Hydrogen with Different Pressures.JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE,10.
MLA	Wang, Huyue,et al."Hydrogen Embrittlement Behavior of X42 Pipeline Steel in Gaseous Hydrogen with Different Pressures".JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE (2024):10.