| Tensile fracture behavior of thermal barrier coatings on superalloy | |
| Z. B. Chen; Z. G. Wang; S. J. Zhu | |
| 2011 | |
| 发表期刊 | Surface & Coatings Technology
 |
| ISSN | 0257-8972 |
| 卷号 | 205期号:15页码:3931-3938 |
| 摘要 | Tensile fracture behavior of thermal barrier coatings (TBCs) on superalloy was investigated in air at room temperature (RT). 650 degrees C and 850 degrees C. The bond coat NiCrAlY was fabricated by either high velocity oxygen fuel (HVOF) or air plasma spraying (APS), and the top coat 7%Y(2)O(3)-ZrO(2) was deposited by APS. Thus two kinds of the TBC system were formed. It was shown that the coating had little effect on tensile stress-strain curves of the substrate and similar tensile strength was obtained in two kinds of the TBC system. However, the cracking behavior in the two kinds of TBC system at RT was different, which was also different from that at 650 degrees C and 850 degrees C by scanning electron microscopy. The interface fracture toughness of the two kinds of TBC system was evaluated by the Suo-Hutchinson model and the stress distribution in the coating and substrate was analyzed by the shear lag model. (C) 2011 Elsevier B.V. All rights reserved. |
| 部门归属 | [chen, z. b.; wang, z. g.] chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china. [zhu, s. j.] fukuoka inst technol, dept intelligent mech engn, higashi ku, fukuoka 8110295, japan.;wang, zg (reprint author), chinese acad sci, inst met res, shenyang natl lab mat sci, 72 wenhua rd, shenyang 110016, peoples r china;zhgwang@imr.ac.cn |
| 关键词 | Thermal Barrier Coating Air Plasma Spraying High Velocity Oxygen Fuel Tensile Fracture Interface Fracture Toughness Mechanical-properties Interface Crack Tbcs |
| URL | 查看原文 |
| WOS记录号 | WOS:000289606000005 |
| 引用统计 | |
| 文献类型 | 期刊论文 |
| 条目标识符 | http://ir.imr.ac.cn/handle/321006/30280 |
| 专题 | 中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Z. B. Chen,Z. G. Wang,S. J. Zhu. Tensile fracture behavior of thermal barrier coatings on superalloy[J]. Surface & Coatings Technology,2011,205(15):3931-3938. |
| APA | Z. B. Chen,Z. G. Wang,&S. J. Zhu.(2011).Tensile fracture behavior of thermal barrier coatings on superalloy.Surface & Coatings Technology,205(15),3931-3938. |
| MLA | Z. B. Chen,et al."Tensile fracture behavior of thermal barrier coatings on superalloy".Surface & Coatings Technology 205.15(2011):3931-3938. |
| 条目包含的文件 | ||||||
| 文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
| Tensile fracture beh（1326KB） | 开放获取 | -- | ||||
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论