A novel method to fabricate titanium aluminum carbides/alumina-laminated composites with weak interfaces was developed through heat treatment titanium aluminum carbides at 1300 degrees C and low oxygen partial pressure. The laminated composites consist of 0.5-mm-thick layers of titanium aluminum carbides joined together by the in situ formed Al(2)O(3) interlayers. The interfaces are free of cracks or delaminations. These laminated materials exhibit better damage tolerance compared with the monolithic counterparts. Crack deflection along the Al(2)O(3) interlayers was the main mechanism for the noncatastrophic failure. The fracture toughness was increased from 4.9 MPa center dot m1/2 for Ti(2)AlC to 7.3 MPa center dot m1/2 for Ti(2)AlC/Al(2)O(3) composite and from 6.5 MPa center dot m1/2 for Ti(3)AlC(2) to 10.4 MPa center dot m1/2 for Ti(3)AlC(2)/Al(2)O(3) composite, and the work of fracture required to break samples was increased from 153 J/m2 for Ti(2)AlC to 676 J/m2 for Ti(2)AlC/Al(2)O(3) composite and from 300 J/m2 for Ti(3)AlC(2) to 1317 J/m2 for Ti(3)AlC(2)/Al(2)O(3) composite.
部门归属
[li, aijun; zhou, yanchun] chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china. [li, aijun] chinese acad sci, grad sch, beijing 100039, peoples r china.;zhou, yc (reprint author), chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china;yczhou@imr.ac.cn
A. J. Li,Y. C. Zhou. A Novel Method to Make Tough Ti(2)AlC/Al(2)O(3)- and Ti(3)AlC(2)/Al(2)O(3)-Laminated Composites[J]. Journal of the American Ceramic Society,2010,93(12):4110-4114.
APA
A. J. Li,&Y. C. Zhou.(2010).A Novel Method to Make Tough Ti(2)AlC/Al(2)O(3)- and Ti(3)AlC(2)/Al(2)O(3)-Laminated Composites.Journal of the American Ceramic Society,93(12),4110-4114.
MLA
A. J. Li,et al."A Novel Method to Make Tough Ti(2)AlC/Al(2)O(3)- and Ti(3)AlC(2)/Al(2)O(3)-Laminated Composites".Journal of the American Ceramic Society 93.12(2010):4110-4114.
修改评论