(Ti(0.5)Nb(0.5))(5)AlC(4): A New-Layered Compound Belonging to MAX Phases

IMR OpenIR

	(Ti(0.5)Nb(0.5))(5)AlC(4): A New-Layered Compound Belonging to MAX Phases
	L. Y. Zheng; J. M. Wang; X. P. Lu; F. Z. Li; J. Y. Wang; Y. C. Zhou
	2010
发表期刊	Journal of the American Ceramic Society
ISSN	0002-7820
卷号	93 期号:10 页码:3068-3071
摘要	A new-layered compound, (Ti(0.5)Nb(0.5))(5)AlC(4), which belongs to MAX phases was discovered. The new-layered carbide was synthesized by reactive hot pressing of Ti, Nb, Al, and C powders. The crystal structure was determined by the combination of X-ray diffraction and transmission electron microscopy analyses, which consists of a 5(Ti, Nb)-C bond chain linked by an Al layer. The lattice parameters are a=3.100 A, c=28.89 A, with Ti(Nb)1 at (0, 0, 0), Ti(Nb)2 at (1/3, 2/3, 0.0877), Ti(Nb)3 at (2/3, 1/3, 0.1723), Al at (0, 0, 0.25), C1 at (2/3, 1/3, 0.0463), and C2 at (0, 0, 0.1566).
部门归属	[zheng, liya; wang, jiemin; lu, xinpo; li, fangzhi; wang, jingyang; zhou, yanchun] chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china. [zheng, liya; wang, jiemin; lu, xinpo; li, fangzhi] chinese acad sci, grad sch, beijing 100039, peoples r china.;zhou, yc (reprint author), chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china;yczhou@imr.ac.cn
关键词	Crystal-structure Ternary Ceramics c System Carbide Ta4alc3 Microstructures Ti3gec2 Ti4aln3 Solids
URL	查看原文
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/31759
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	L. Y. Zheng,J. M. Wang,X. P. Lu,et al. (Ti(0.5)Nb(0.5))(5)AlC(4): A New-Layered Compound Belonging to MAX Phases[J]. Journal of the American Ceramic Society,2010,93(10):3068-3071.
APA	L. Y. Zheng,J. M. Wang,X. P. Lu,F. Z. Li,J. Y. Wang,&Y. C. Zhou.(2010).(Ti(0.5)Nb(0.5))(5)AlC(4): A New-Layered Compound Belonging to MAX Phases.Journal of the American Ceramic Society,93(10),3068-3071.
MLA	L. Y. Zheng,et al."(Ti(0.5)Nb(0.5))(5)AlC(4): A New-Layered Compound Belonging to MAX Phases".Journal of the American Ceramic Society 93.10(2010):3068-3071.