Influence of NaCl deposition on atmospheric corrosion behavior of AZ91 magnesium alloy

IMR OpenIR

	Influence of NaCl deposition on atmospheric corrosion behavior of AZ91 magnesium alloy
	W. Q. Zhou; D. Y. Shan; E. H. Han; W. Ke
	2010
发表期刊	Transactions of Nonferrous Metals Society of China
ISSN	1003-6326
卷号	20 页码:S670-S673
摘要	Corrosion behavior of AZ91 magnesium alloy under NaCl particle deposition condition was investigated by gravimetric method and surface analysis technique. It was found that the mass gain increased rapidly at the beginning of exposure and then slowly with time. The corrosion morphologies were observed and the results showed that NaCl deposition resulted in the occurrence of localized corrosion. The composition of corrosion product was analyzed using X-ray photo electron spectroscopy. It was suggested that the corrosion product was a mixture of oxide and hydroxide of magnesium and aluminum.
部门归属	[zhou wan-qiu] shenyang normal univ, coll chem & life sci, shenyang 110034, peoples r china. [zhou wan-qiu; shan da-yong; han en-hou; ke wei] chinese acad sci, inst met res, state key lab corros & protect, shenyang 110016, peoples r china.;zhou, wq (reprint author), shenyang normal univ, coll chem & life sci, shenyang 110034, peoples r china;wqzhou@imr.ac.cn
关键词	Magnesium Alloy Atmospheric Corrosion Nacl Deposition X-ray Photo Electron Spectroscopy Chloride Humidity
URL	查看原文
WOS记录号	WOS:000280873300073
引用统计	被引频次：13[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/31779
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	W. Q. Zhou,D. Y. Shan,E. H. Han,et al. Influence of NaCl deposition on atmospheric corrosion behavior of AZ91 magnesium alloy[J]. Transactions of Nonferrous Metals Society of China,2010,20:S670-S673.
APA	W. Q. Zhou,D. Y. Shan,E. H. Han,&W. Ke.(2010).Influence of NaCl deposition on atmospheric corrosion behavior of AZ91 magnesium alloy.Transactions of Nonferrous Metals Society of China,20,S670-S673.
MLA	W. Q. Zhou,et al."Influence of NaCl deposition on atmospheric corrosion behavior of AZ91 magnesium alloy".Transactions of Nonferrous Metals Society of China 20(2010):S670-S673.