| Formation of hydrogen blister on AZ91 magnesium alloy during cathodic charging | |
| J. Chen; M. R. Ai; J. Q. Wang; E. H. Han; W. Ke | |
| 2009 | |
| 发表期刊 | Corrosion Science
 |
| ISSN | 0010-938X |
| 卷号 | 51期号:5页码:1197-1200 |
| 摘要 | The process of hydrogen blister formation on as-cast AZ91 magnesium alloy was investigated in 0.1 M NaOH solution using galvanostatic test. The results showed that cathodic charging of AZ91 alloy resulted in hydrogen blister formation, and blister rupture caused the nucleation and propagation of transgranular micro-cracks around the ruptured blister. (C) 2009 Elsevier Ltd. All rights reserved. |
| 部门归属 | [chen, jian; ai, meirong; wang, jianqiu; han, en-hou; ke, wei] chinese acad sci, inst met res, state key lab corros & protect, shenyang 110016, liaoning, peoples r china.;wang, jq (reprint author), chinese acad sci, inst met res, state key lab corros & protect, wencui rd 62, shenyang 110016, liaoning, peoples r china;jiqwang@imr.ac.cn |
| 关键词 | Magnesium Galvanostatic Stress-corrosion Cracking In-situ Observation Mg-al Alloy Sodium-sulfate Solution Wet-dry Conditions Na2so4 Solution Behavior Initiation Hydride Steels |
| URL | 查看原文 |
| WOS记录号 | WOS:000266532600032 |
| 引用统计 | |
| 文献类型 | 期刊论文 |
| 条目标识符 | http://ir.imr.ac.cn/handle/321006/31824 |
| 专题 | 中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | J. Chen,M. R. Ai,J. Q. Wang,et al. Formation of hydrogen blister on AZ91 magnesium alloy during cathodic charging[J]. Corrosion Science,2009,51(5):1197-1200. |
| APA | J. Chen,M. R. Ai,J. Q. Wang,E. H. Han,&W. Ke.(2009).Formation of hydrogen blister on AZ91 magnesium alloy during cathodic charging.Corrosion Science,51(5),1197-1200. |
| MLA | J. Chen,et al."Formation of hydrogen blister on AZ91 magnesium alloy during cathodic charging".Corrosion Science 51.5(2009):1197-1200. |
| 条目包含的文件 | ||||||
| 文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
| 1592.pdf（360KB） | 开放获取 | -- | ||||
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论