Synthesis and compressive properties of Al-Ni-Y metallic glass

IMR OpenIR

	Synthesis and compressive properties of Al-Ni-Y metallic glass
	H. M. Fu; J. Mu; A. M. Wang; H. Li; Z. Q. Hu; H. F. Zhang
	2009
发表期刊	Philosophical Magazine Letters
ISSN	0950-0839
卷号	89 期号:11 页码:711-716
摘要	An Al-based metallic glass rod with 0.75 mm diameter was prepared successfully using the copper-mould casting technique together with the proper melt treatment of the liquid alloy. The compressive properties of this Al-Ni-Y metallic glass were experimentally examined. The results showed that the amorphous alloy has a high yield strength of 1090 MPa and a compressive fracture strength of 1150 MPa. Its fracture surface presented typical vein patterns and melting phenomena characteristic of a monolithic metallic glass.
部门归属	[fu, h. m.; mu, j.; wang, a. m.; li, h.; hu, z. q.; zhang, h. f.] chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china. [mu, j.] chinese acad sci, grad sch, beijing 100039, peoples r china.;zhang, hf (reprint author), chinese acad sci, inst met res, shenyang natl lab mat sci, 72 wenhua rd, shenyang 110016, peoples r china;hfzhang@imr.ac.cn
关键词	Al-based Metallic Glass Casting Compressive Strength Forming Ability Range Order Alloys
URL	查看原文
WOS记录号	WOS:000271570300006
引用统计	被引频次：13[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/31907
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	H. M. Fu,J. Mu,A. M. Wang,et al. Synthesis and compressive properties of Al-Ni-Y metallic glass[J]. Philosophical Magazine Letters,2009,89(11):711-716.
APA	H. M. Fu,J. Mu,A. M. Wang,H. Li,Z. Q. Hu,&H. F. Zhang.(2009).Synthesis and compressive properties of Al-Ni-Y metallic glass.Philosophical Magazine Letters,89(11),711-716.
MLA	H. M. Fu,et al."Synthesis and compressive properties of Al-Ni-Y metallic glass".Philosophical Magazine Letters 89.11(2009):711-716.