Influence of Al Content on the Atmospheric Corrosion Behaviour of Magnesium-Aluminum Alloys

IMR OpenIR

	Influence of Al Content on the Atmospheric Corrosion Behaviour of Magnesium-Aluminum Alloys
	R. L. Jia; C. W. Yan; F. H. Wang
	2009
发表期刊	Journal of Materials Science & Technology
ISSN	1005-0302
卷号	25 期号:2 页码:225-229
摘要	The influence of Al content on the Mg-Al alloys corrosion performance during sodium chloride induced atmospheric corrosion has been studied. It was found that the corrosion rate of three Mg-Al alloys was accelerated with increasing N content. The poor corrosion resistance was attributed to the galvanic coupling between the beta phase and eutectic phase or a phase and the formation of porous corrosion products.
部门归属	[jia, ruiling; wang, fuhui] harbin engn univ, key lab superlight mat & surface technol, minist educ, coll mat sci & chem engn, harbin 150001, peoples r china. [yan, chuanwei; wang, fuhui] chinese acad sci, inst met res, state key lab corros & protect, shenyang 110016, peoples r china. [jia, ruiling] inner mongolia univ technol, coll mat sci & engn, hohhot 010051, peoples r china.;jia, rl (reprint author), harbin engn univ, key lab superlight mat & surface technol, minist educ, coll mat sci & chem engn, harbin 150001, peoples r china;jrl014014@163.com
关键词	Magnesium Alloys Al Content Atmospheric Corrosion Sodium-chloride Az91 Nacl Microstructure Deposition Phase Co2
URL	查看原文
WOS记录号	WOS:000264990700017
引用统计	被引频次：6[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/31995
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	R. L. Jia,C. W. Yan,F. H. Wang. Influence of Al Content on the Atmospheric Corrosion Behaviour of Magnesium-Aluminum Alloys[J]. Journal of Materials Science & Technology,2009,25(2):225-229.
APA	R. L. Jia,C. W. Yan,&F. H. Wang.(2009).Influence of Al Content on the Atmospheric Corrosion Behaviour of Magnesium-Aluminum Alloys.Journal of Materials Science & Technology,25(2),225-229.
MLA	R. L. Jia,et al."Influence of Al Content on the Atmospheric Corrosion Behaviour of Magnesium-Aluminum Alloys".Journal of Materials Science & Technology 25.2(2009):225-229.