Effect of Hydrogen on Fatigue Strength of High-Strength Steels in the VHCF Regime

IMR OpenIR

	Effect of Hydrogen on Fatigue Strength of High-Strength Steels in the VHCF Regime
	Y. D. Li; Z. G. Yang; S. X. Li; Y. B. Liu; S. M. Chen; W. J. Hui; Y. Q. Weng
	2009
发表期刊	Advanced Engineering Materials
ISSN	1438-1656
卷号	11 期号:7 页码:561-567
部门归属	[li, yongde; yang, zhenguo; li, shouxin; liu, yangbo; chen, shuming] chinese acad sci, shenyang natl lab mat sci, inst met res, shenyang 110016, peoples r china. [hui, weijun; weng, yuqing] cent iron & steel res inst, beijing 100081, peoples r china.;li, yd (reprint author), chinese acad sci, shenyang natl lab mat sci, inst met res, shenyang 110016, peoples r china;ydl@imr.ac.cn
关键词	Subsurface Crack Initiation Long Cycle Fatigue N-greater-than-10(7) Cycles Gigacycle Fatigue Assisted Cracking Part Ii Mechanism Failure Life Inclusions
URL	查看原文
WOS记录号	WOS:000269090500008
引用统计	被引频次：28[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/32046
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	Y. D. Li,Z. G. Yang,S. X. Li,et al. Effect of Hydrogen on Fatigue Strength of High-Strength Steels in the VHCF Regime[J]. Advanced Engineering Materials,2009,11(7):561-567.
APA	Y. D. Li.,Z. G. Yang.,S. X. Li.,Y. B. Liu.,S. M. Chen.,...&Y. Q. Weng.(2009).Effect of Hydrogen on Fatigue Strength of High-Strength Steels in the VHCF Regime.Advanced Engineering Materials,11(7),561-567.
MLA	Y. D. Li,et al."Effect of Hydrogen on Fatigue Strength of High-Strength Steels in the VHCF Regime".Advanced Engineering Materials 11.7(2009):561-567.