Computer simulation of core filling process of cast high speed steel roll

IMR OpenIR

	Computer simulation of core filling process of cast high speed steel roll; Computer simulation of core filling process of cast high speed steel roll
	N. N. Song; Y. K. Luan; Y. L. Bai; X. H. Kang; L. J. Xia; D. Z. Li
	2009 ; 2009
发表期刊	China Foundry ; China Foundry
ISSN	1672-6421 ; 1672-6421
卷号	6 期号:4 页码:314-318
摘要	Core filling process of cast high speed steel roll was simulated. Ductile iron was used as core material. The influence of filling parameters, such as core filling time and core filling temperature, on the filling process were investigated. Based on the simulated results, optimal core filling parameters were determined. The predicted temperature fields show that the temperature at the roll shoulder is the lowest during the core filling process and usually causes binding defects there. Method for solving this problem was presented.; Core filling process of cast high speed steel roll was simulated. Ductile iron was used as core material. The influence of filling parameters, such as core filling time and core filling temperature, on the filling process were investigated. Based on the simulated results, optimal core filling parameters were determined. The predicted temperature fields show that the temperature at the roll shoulder is the lowest during the core filling process and usually causes binding defects there. Method for solving this problem was presented.
部门归属	[song nannan; luan yikun; bai yunlong; kang xiuhong; xia lijun; li dianzhong] chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china.;kang, xh (reprint author), chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china, peoples r china;xhkang@imr.ac.cn ; [song nannan; luan yikun; bai yunlong; kang xiuhong; xia lijun; li dianzhong] chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china.;kang, xh (reprint author), chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china, peoples r china;xhkang@imr.ac.cn
关键词	Computer Simulation Computer Simulation Higher Speed Steel Roll Higher Speed Steel Roll Core Filling Core Filling Bindind Bindind Layer Layer
URL	查看原文 ; 查看原文
WOS记录号	WOS:000272457700005 ; WOS:000272457700005
引用统计	被引频次：7[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/32288
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	N. N. Song,Y. K. Luan,Y. L. Bai,et al. Computer simulation of core filling process of cast high speed steel roll, Computer simulation of core filling process of cast high speed steel roll[J]. China Foundry, China Foundry,2009, 2009,6, 6(4):314-318, 314-318.
APA	N. N. Song,Y. K. Luan,Y. L. Bai,X. H. Kang,L. J. Xia,&D. Z. Li.(2009).Computer simulation of core filling process of cast high speed steel roll.China Foundry,6(4),314-318.
MLA	N. N. Song,et al."Computer simulation of core filling process of cast high speed steel roll".China Foundry 6.4(2009):314-318.