Molten Salt Synthesis of Magnesium Aluminate (MgAl(2)O(4)) Spinel on Ti(3)AlC(2) Substrate

IMR OpenIR

	Molten Salt Synthesis of Magnesium Aluminate (MgAl(2)O(4)) Spinel on Ti(3)AlC(2) Substrate
	J. Zhang; D. H. Li; Y. C. Zhou
	2009
发表期刊	Journal of the American Ceramic Society
ISSN	0002-7820
卷号	92 期号:5 页码:1074-1078
摘要	A MgAl(2)O(4) (MA) spinel layer was synthesized on Ti(3)AlC(2) substrate through the molten salt synthesis (MSS) method. The Ti(3)AlC(2) substrate was immersed in MgCl(2)center dot 6H(2)O powders and treated at 8001, 8501, and 900 degrees C for 4 h in air. A continuous and 10-mu m-thick MgAl(2)O(4) layer was obtained at 900 degrees C, by which the surface hardness of Ti(3)AlC(2) can be effectively improved. The combined scanning electron microscopy observations and crystal morphology simulation further revealed that the as-formed MgAl(2)O(4) presents tetragonal bipyramids morphology with (400)-orientation.
部门归属	[zhang, jie; li, danhua; zhou, yanchun] chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china. [zhang, jie] chinese acad sci, grad sch, beijing 100039, peoples r china.;zhou, yc (reprint author), chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, peoples r china;yczhou@imr.ac.cn
关键词	Liquid Reaction Synthesis Oxide Scale Ti3sic2 Microstructure Precursors Resistance Diffusion Platelet Adhesion Behavior
URL	查看原文
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/32545
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	J. Zhang,D. H. Li,Y. C. Zhou. Molten Salt Synthesis of Magnesium Aluminate (MgAl(2)O(4)) Spinel on Ti(3)AlC(2) Substrate[J]. Journal of the American Ceramic Society,2009,92(5):1074-1078.
APA	J. Zhang,D. H. Li,&Y. C. Zhou.(2009).Molten Salt Synthesis of Magnesium Aluminate (MgAl(2)O(4)) Spinel on Ti(3)AlC(2) Substrate.Journal of the American Ceramic Society,92(5),1074-1078.
MLA	J. Zhang,et al."Molten Salt Synthesis of Magnesium Aluminate (MgAl(2)O(4)) Spinel on Ti(3)AlC(2) Substrate".Journal of the American Ceramic Society 92.5(2009):1074-1078.