The effect of magnetic field heat treatment on magnetostriction of Terfenol-D 2-2 composites

IMR OpenIR

	The effect of magnetic field heat treatment on magnetostriction of Terfenol-D 2-2 composites
	S. Y. Li; B. W. Wang; L. Weng; Y. Zhou; Y. Sun; W. M. Huang
	2008
发表期刊	Journal of Magnetism and Magnetic Materials
ISSN	0304-8853
卷号	320 期号:6 页码:806-809
摘要	Based on the analysis of the magnetostriction for Terfenol-D composites, Terfenol-D 2-2 magnetostrictive composites have been prepared with laminations perpendicular to [1 1 2] axes. Then one of the samples was annealed in the vacuum at 423K for 15 min at the magnetic field of 240 kA/m, which is along the direction of laminations and vertical to the [1 1 2] axes of the specimen. The static magnetostriction l and dynamic magnetostrictive lambda coefficient d(33) of samples were measured under the compressive stress of 0, 2, 4, 6 and 8 MPa. Effects of the compressive stress and the magnetic field heat treatment on the magnetostriction lambda have been investigated. It is found that the magnetostriction of 2-2 composites can be improved under the compressive stress when the magnetic field is larger than 20 kA/m. The magnetostriction of 2-2 composites with the magnetic field heat treatment increases under compressive stress, and it can reach 1390x10(-6) at the magnetic field of 200 kA/m and under the compressive stress of 4 MPa, much larger than the value of 860x10(-6) without the magnetic field heat treatment. The highest magnetostriction of the 2-2 composite with the magnetic field heat treatment can reach 1530x10(-6). The dynamic magnetostrictive coefficient d(33) of 2-2 composites with the magnetic field heat treatment have been improved, compared with that without magnetic field heat treatment. The maximum value of d(33) of the sample with magnetic field heat treatment is 71% larger than that without magnetic field heat treatment. (C) 2007 Elsevier B.V. All rights reserved.
部门归属	[li, s. y.; wang, b. w.; weng, l.; zhou, y.; sun, y.; huang, w. m.] hebei univ technol, sch elect engn, prov minist joint key lab electromagnet field & e, tianjin 300130, peoples r china. [li, s. y.] tianjin univ technol, sch sci, tianjin 300160, peoples r china. [wang, b. w.] acad sinica, int ctr mat phys, shenyang 110015, peoples r china.;li, sy (reprint author), hebei univ technol, sch elect engn, prov minist joint key lab electromagnet field & e, tianjin 300130, peoples r china;shylicl@126.com
关键词	Terfenol-d 2-2 Composite Magnetostriction Dynamic Magnetostrictive Coefficient Compressive Stress Magnetic Field Heat Treatment Tb0.27dy0.73fe2 Single-crystal
URL	查看原文
WOS记录号	WOS:000254416300008
引用统计	被引频次：7[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/32895
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	S. Y. Li,B. W. Wang,L. Weng,et al. The effect of magnetic field heat treatment on magnetostriction of Terfenol-D 2-2 composites[J]. Journal of Magnetism and Magnetic Materials,2008,320(6):806-809.
APA	S. Y. Li,B. W. Wang,L. Weng,Y. Zhou,Y. Sun,&W. M. Huang.(2008).The effect of magnetic field heat treatment on magnetostriction of Terfenol-D 2-2 composites.Journal of Magnetism and Magnetic Materials,320(6),806-809.
MLA	S. Y. Li,et al."The effect of magnetic field heat treatment on magnetostriction of Terfenol-D 2-2 composites".Journal of Magnetism and Magnetic Materials 320.6(2008):806-809.