Synergistic corrosion behavior of coated Ti60 alloys with NaCl deposit in moist air at elevated temperature

IMR OpenIR

	Synergistic corrosion behavior of coated Ti60 alloys with NaCl deposit in moist air at elevated temperature
	Y. M. Xiong; S. L. Zhu; F. H. Wang
	2008
发表期刊	Corrosion Science
ISSN	0010-938X
卷号	50 期号:1 页码:15-22
摘要	In the present paper, the corrosion behavior of Ti60 alloys with an aluminide, TiAlCr, and enamel coatings in moist air containing NaCl vapor at 700-800 degrees C were studied. The results showed that the TiAlCr and aluminide coatings failed to protect the substrate from corrosion due to the cyclic formation of volatile products during corrosion at 800 degrees C. However, an uneven continuous protective Al2O3 scale could form on the aluminide coating during corrosion at 700 degrees C. And the enamel coating could protect Ti60 from corrosion due to its high thermochernical stability and matched thermal expansion coefficient with substrates of Ti-base alloys during corrosion. (c) 2007 Elsevier Ltd. All rights reserved.
部门归属	[xiong, yuming; zhu, shenglong; wang, fuhui] chinese acad sci, state key lab corros & protect, shenyang 110016, peoples r china.;xiong, ym (reprint author), chinese acad sci, state key lab corros & protect, wencui rd 62, shenyang 110016, peoples r china;ymxiong@imr.ac.cn fhwang@imr.ac.cn
关键词	Titanium Metal Coatings X-ray Diffraction High Temperature Corrosion Oxide Coatings Alumina Scale Formation Oxide hydrOxide Evaporation Al-cr Alloys Oxidation Behavior Water-vapor Titanium Aluminides Cyclic Oxidation Coatings Chromium Intermetallics
URL	查看原文
WOS记录号	WOS:000253093100004
引用统计	被引频次：51[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/33238
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	Y. M. Xiong,S. L. Zhu,F. H. Wang. Synergistic corrosion behavior of coated Ti60 alloys with NaCl deposit in moist air at elevated temperature[J]. Corrosion Science,2008,50(1):15-22.
APA	Y. M. Xiong,S. L. Zhu,&F. H. Wang.(2008).Synergistic corrosion behavior of coated Ti60 alloys with NaCl deposit in moist air at elevated temperature.Corrosion Science,50(1),15-22.
MLA	Y. M. Xiong,et al."Synergistic corrosion behavior of coated Ti60 alloys with NaCl deposit in moist air at elevated temperature".Corrosion Science 50.1(2008):15-22.