| Improved capacitance of SBA-15 templated mesoporous carbons after modification with nitric acid oxidation | |
| D. W. Wang; F. Li; M. Liu; H. M. Cheng | |
| 2007 | |
| Source Publication | New Carbon Materials
 |
| ISSN | 1007-8827 |
| Volume | 22Issue:4Pages:307-314 |
| Abstract | This study reports modified SBA-15 templated mesoporous carbon as a supercapacitor electrode for high-efficiency energy storage. Mesoporous carbon was oxidized in concentrated nitric acid at 26 degrees C, 50 degrees C, 70 degrees C, and 100 degrees C. The evolution of mesopores and surface oxygen-containing functional groups (SOFGs) of the mesoporous carbons were studied by nitrogen cryosorption, X-ray photoelectron spectroscopy, and thenno-gravimetric analysis. The results demonstrate that the specific surface area and the mesopore volume decrease, while the SOFGs accumulate with increasing oxidation temperature. The supercapacitor performance Was characterized in a KOH aqueous electrolyte. An enhanced energy density with a highest value of 5.7Wh/kg is obtained after oxidation at 100 degrees C compared to 3.5Wh/kg before oxidation, demonstrating the possibility of using modified mesoporous carbons in high energy density applications. The enhanced energy density is attributed to the contribution of SOFGs to charge storage in both the electric double layer and the Faradic reaction. The power density is also improved with a highest value of 3 125 W/kg after oxidation at 76 degrees C compared to the original value of 2 015 W/kg. The improvement of power density relies on the improved wettability of carbon surfaces, which can facilitate the ion transport. |
| description.department | [wang da-wei; li feng; liu min; cheng hui-ming] chinese acad sci, shenyang natl lab mat sci, inst met res, shenyang 110016, peoples r china.;cheng, hm (reprint author), chinese acad sci, shenyang natl lab mat sci, inst met res, shenyang 110016, peoples r china;dwwang@imr.ac.cn cheng@imr.ac.cn |
| Keyword | Mesoporous Carbon Surface Oxygen Functional Groups Electrochemical Properties Double-layer Capacitance Activated Carbons Edlc Performance Electrodes Chemistry |
| URL | 查看原文 |
| WOS ID | WOS:000252044000004 |
| Citation statistics | |
| Document Type | 期刊论文 |
| Identifier | http://ir.imr.ac.cn/handle/321006/33853 |
| Collection | 中国科学院金属研究所 |
| Recommended Citation GB/T 7714 | D. W. Wang,F. Li,M. Liu,et al. Improved capacitance of SBA-15 templated mesoporous carbons after modification with nitric acid oxidation[J]. New Carbon Materials,2007,22(4):307-314. |
| APA | D. W. Wang,F. Li,M. Liu,&H. M. Cheng.(2007).Improved capacitance of SBA-15 templated mesoporous carbons after modification with nitric acid oxidation.New Carbon Materials,22(4),307-314. |
| MLA | D. W. Wang,et al."Improved capacitance of SBA-15 templated mesoporous carbons after modification with nitric acid oxidation".New Carbon Materials 22.4(2007):307-314. |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment