| Corrosion behavior on aluminum alloy LY12 in simulated atmospheric corrosion process |
| Z. Y. Wang; T. Ma; W. Han; G. C. Yu
|
| 2007
|
| 发表期刊 | Transactions of Nonferrous Metals Society of China
 |
| ISSN | 1003-6326
|
| 卷号 | 17期号:2页码:326-334 |
| 摘要 | The corrosion behavior of typical high-strength aluminum alloy LY 12 was studied by accelerated corrosion tests of cyclic wet-dry-immersion containing media of NaHSO3 and NaCl to simulate the corrosion process in different atmosphere environment, and the corrosion mechanism was also discussed. The main experimental techniques include mass loss, morphological check, analysis of corrosion products and electrochemical measurement. The result shows that the mass loss of LY12, with or without cladding, has linear relationship with test time in the three kinds of chemical media, 0.02 mol/L NaHSO3, 0.006 mol/L NaCl and 0.02 mol/L NaHSO3+0.006 mol/L NaCl, respectively. A layer of cladding on high-strength aluminum alloy can raise evidently the resistance of atmospheric corrosion. Cl- can promote pitting generation on the oxide film of LY12 when HOS3- exists, LY12 can react much intensely with HOS3- derived from anions. |
| 部门归属 | chinese acad sci, environm corros ctr, inst met res, shenyang 110016, peoples r china.;wang, zy (reprint author), chinese acad sci, environm corros ctr, inst met res, shenyang 110016, peoples r china;zhywang@imr.ac.cn
|
| 关键词 | Aluminum Alloy
Atmospheric Corrosion
Accelerated Corrosion Test
Surface Analysis
Electrochemical Measure
|
| URL | 查看原文
|
| WOS记录号 | WOS:000246509900019
|
| 引用统计 |
|
| 文献类型 | 期刊论文
|
| 条目标识符 | http://ir.imr.ac.cn/handle/321006/33890
|
| 专题 | 中国科学院金属研究所
|
推荐引用方式
GB/T 7714 |
Z. Y. Wang,T. Ma,W. Han,et al. Corrosion behavior on aluminum alloy LY12 in simulated atmospheric corrosion process[J]. Transactions of Nonferrous Metals Society of China,2007,17(2):326-334.
|
| APA |
Z. Y. Wang,T. Ma,W. Han,&G. C. Yu.(2007).Corrosion behavior on aluminum alloy LY12 in simulated atmospheric corrosion process.Transactions of Nonferrous Metals Society of China,17(2),326-334.
|
| MLA |
Z. Y. Wang,et al."Corrosion behavior on aluminum alloy LY12 in simulated atmospheric corrosion process".Transactions of Nonferrous Metals Society of China 17.2(2007):326-334.
|
修改评论