Topologically close-packed phase precipitation in a nickel-base superalloy during thermal exposure

IMR OpenIR

	Topologically close-packed phase precipitation in a nickel-base superalloy during thermal exposure
	J. X. Yang; Q. Zheng; X. F. Sun; H. R. Guan; Z. Q. Hu
	2007
发表期刊	Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing
ISSN	0921-5093
卷号	465 期号:1-2 页码:100-108
摘要	K465 superalloy was thermally exposed, respectively at 850, 950, 1000, 1050 and 1100 degrees C. During thermal exposure, topologically close-packed phases, such as sigma and mu, are precipitated in interdendritic regions where rapid diffusion paths are provided and the TCP forming elements W, Mo, Cr, Co are concentrated. The exposure temperature is shown to have a great impact on the formation and growth of TCP phases. a phase is readily formed at the lower annealing temperature (below 950 degrees C), having a basket weave or multi-layer structure whereas becomes instable at the higher exposure temperature above 950 degrees C. The disappearance of mu phase at higher temperature mainly results from the formation of M23C6 and M6C carbides because they can combine with the larger amounts of the a forming element, Cr. The precipitation of mu phase is mainly depended on M6C carbide, and its morphology exhibits coarse needles or platelets. mu phase is stable above 950 degrees C, and the amount of mu phase reaches the peak value at 1000 degrees C, but is decreased above 1000 degrees C. (C) 2007 Elsevier B.V. All rights reserved.
部门归属	chinese acad sci, dept superalloys, inst met res, shenyang 110016, peoples r china.;yang, jx (reprint author), chinese acad sci, dept superalloys, inst met res, 72 wenhua rd, shenyang 110016, peoples r china;jxyang@imr.ac.cn
关键词	Superalloy Thermal Exposure Topologically Close-packed Phases Carbide Sx-superalloys Tcp Phases Crystal Additions
URL	查看原文
WOS记录号	WOS:000248637600015
引用统计	被引频次：116[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/33970
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	J. X. Yang,Q. Zheng,X. F. Sun,et al. Topologically close-packed phase precipitation in a nickel-base superalloy during thermal exposure[J]. Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing,2007,465(1-2):100-108.
APA	J. X. Yang,Q. Zheng,X. F. Sun,H. R. Guan,&Z. Q. Hu.(2007).Topologically close-packed phase precipitation in a nickel-base superalloy during thermal exposure.Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing,465(1-2),100-108.
MLA	J. X. Yang,et al."Topologically close-packed phase precipitation in a nickel-base superalloy during thermal exposure".Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing 465.1-2(2007):100-108.