Enhancement of paramagnetic defects in yttria stabilized zirconia implanted by Cs ion irradiation

IMR OpenIR

	Enhancement of paramagnetic defects in yttria stabilized zirconia implanted by Cs ion irradiation
	X. T. Zu; S. Zhu; L. M. Wang; R. C. Ewing
	2007
发表期刊	Journal of Alloys and Compounds
ISSN	0925-8388
卷号	429 期号:1-2 页码:25-28
摘要	Single crystal samples of cubic zirconia stabilized by 9.5 mol% Y2O3 (YSZ) were implanted with 200 KeV Xe ions and 400 KeV Cs ions up to a dose of 5 x 10(16) ions/cm(2), then annealed at 200, 300, and 400 degrees C for 1 h isochronously, respectively. Electron paramagnetic resonance (EPR) and cross-sectional transmission electron microscopy were used to study defect structure and radiated damage mechanism. EPR spectra showed the trigonal signal with g(parallel to) = 1.989 and g(perpendicular to) = 1.869, which exhibited axial symmetry with (111) direction as symmetry axis composed of six-fold-coordinated Zr3+ sites. Peak-to-peak intensity (per unit volume) of Cs-ion irradiated YSZ is as about 150 time as that of Xe-ion irradiated YSZ. This indicated that the concentration of six-fold-coordinated Zr3+ defects produced by Cs-ion irradiation was far more than that of Xe-ion irradiated. The cross-sectional image of the irradiated samples showed that the Cs-ion irradiation in YSZ produced more defect clusters than Xe-ion irradiation. Annealing did not produce any change for EPR signals and indicated six-fold-coordinated Zr3+ defects was stable defect structure below 400 degrees C. (c) 2006 Elsevier B.V. All rights reserved.
部门归属	univ elect sci & technol china, dept appl phys, chengdu 610054, peoples r china. chinese acad sci, int ctr mat phys, shenyang 110015, peoples r china. univ michigan, dept nucl engn & radiol sci, ann arbor, mi 48109 usa.;zu, xt (reprint author), univ elect sci & technol china, dept appl phys, chengdu 610054, peoples r china;xiaotaozu@yahoo.com
关键词	Yttria Stabilized Zirconia Heavy Ion irradiatIon Tem Electron Paramagnetic Resonance Radiation-damage Single-crystals Phase-transition Cubic Zirconia Electron Traps Epr Centers Glasses Nanocrystals Resonance
URL	查看原文
WOS记录号	WOS:000244673100005
引用统计	被引频次：8[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/34121
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	X. T. Zu,S. Zhu,L. M. Wang,et al. Enhancement of paramagnetic defects in yttria stabilized zirconia implanted by Cs ion irradiation[J]. Journal of Alloys and Compounds,2007,429(1-2):25-28.
APA	X. T. Zu,S. Zhu,L. M. Wang,&R. C. Ewing.(2007).Enhancement of paramagnetic defects in yttria stabilized zirconia implanted by Cs ion irradiation.Journal of Alloys and Compounds,429(1-2),25-28.
MLA	X. T. Zu,et al."Enhancement of paramagnetic defects in yttria stabilized zirconia implanted by Cs ion irradiation".Journal of Alloys and Compounds 429.1-2(2007):25-28.