Microstructure and mechanical properties of a 2000 MPa grade co-free maraging steel

IMR OpenIR

	Microstructure and mechanical properties of a 2000 MPa grade co-free maraging steel
	Y. He; K. Yang; W. Sha
	2005
发表期刊	Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science
ISSN	1073-5623
卷号	36A 期号:9 页码:2273-2287
摘要	The precipitation kinetics in the aging temperature range of 713 to 813 K in a 2000 MPa grade Co-free maraging steel (Fe-18.9 pct Ni-4.1 pet Mo-1.9 pet Ti, mass pct) has been studied. Study on microstructure and mechanical properties showed that a great deal of Ni3Ti and a type of unknown spheroidal precipitates both with average diameter of 2 to 3 nm are formed in the early aging stage at 713 K, which results in a high strength and a relatively low fracture toughness. Ni3Ti precipitates grow into needle or rod shape and become the main precipitation as the aging time is prolonged. Strength increases and fracture toughness (K-1C) decreases with growth of the precipitates. The ultra-high strength of the maraging steel subjected to long-time aging at 713 K is attributed to the high resistance to coarsening of the precipitates. The strengthening in the underaged condition at 713 K is a combination of dislocations cutting through precipitates and the Orowan mechanisms. Aged at 813 K, the size of Ni3Ti precipitates is seriously nonuniform at the early stage and a small amount of interlath reverted austenite is formed. Thereafter, Ni3Ti precipitates coarsen sharply accompanied with the embrittlement. Intralath reverted austenite appears subsequently. In the later stage of aging, the coarsened Ni3Ti precipitates dissolve into the striplike intralath reverted austenite that is disorderly embedded in the matrix. All of these result in a low strength and low fracture toughness under overaging condition. Analysis shows that the formation of reverted austenite contains the diffusion and Kudjumov-Sachs (K-S) and Nishiyama-Wassermann (N-W) shear mechanisms.
部门归属	chinese acad sci, inst met res, shenyang 110016, peoples r china. delft univ technol, mat sci lab, nl-2628 al delft, netherlands. queens univ belfast, sch civil engn architecture & planning, mat res grp, belfast bt7 1nn, antrim, north ireland.;he, y (reprint author), chinese acad sci, inst met res, shenyang 110016, peoples r china;w.sha@qub.ac.uk
关键词	Precipitation Reactions Phase Chemistry Transformation Plasticity Fracture-toughness Reverted Austenite Aging Behavior Ni Alloys Mo
URL	查看原文
WOS记录号	WOS:000231396600001
引用统计	被引频次：60[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/34871
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	Y. He,K. Yang,W. Sha. Microstructure and mechanical properties of a 2000 MPa grade co-free maraging steel[J]. Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science,2005,36A(9):2273-2287.
APA	Y. He,K. Yang,&W. Sha.(2005).Microstructure and mechanical properties of a 2000 MPa grade co-free maraging steel.Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science,36A(9),2273-2287.
MLA	Y. He,et al."Microstructure and mechanical properties of a 2000 MPa grade co-free maraging steel".Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science 36A.9(2005):2273-2287.