| Corrosion inhibitor performances for carbon dioxide corrosion of N80 steel under static and flowing conditions | |
| X. Jiang; Y. G. Zheng; W. Ke | |
| 2005 | |
| Source Publication | Corrosion
 |
| ISSN | 0010-9312 |
| Volume | 61Issue:4Pages:326-334 |
| Abstract | Inhibition for carbon dioxide (CO2) corrosion of N80 steel by quaternary alkynoxymethyl amine (IMC-80-Q) in 3% sodium chloride (NaCl) solution was investigated under static and flowing conditions using a modified rotating disk apparatus. The effects of flow velocity and concentration of inhibitor on inhibition performance were performed using a weight-loss test, scanning electron microscope (SEM) observation, and electrochemical techniques including electrochemical impedance spectroscopy (EIS), linear polarization resistance, and polarization curves. The results showed that flow velocity had strong effects on the inhibitor performances. Inhibition efficiency (q) and polarization resistance (R) exhibited the peak-value phenomenon at an inhibitor concentration of 150 mg/L when flow velocity was less than 5 m/s, in contrast with the 300 mg/L when flow velocity was higher than 5 m/s. Critical flow velocity in the uninhibited solution was between 4 m/s and 5 m/s. |
| description.department | chinese acad sci, met res inst, state key lab corros & protect, shenyang 110016, liaoning prov, peoples r china.;zheng, yg (reprint author), chinese acad sci, met res inst, state key lab corros & protect, 62 wencui rd, shenyang 110016, liaoning prov, peoples r china;ygzheng@imr.ac.cn |
| Keyword | Carbon Dioxide Corrosion Criticalflow Velocity Flow Effect Inhibitor N80 Steel Peak-value Phenomenon Impedance Plane Displays Rotating Cylinder Stability Conditions Steady-state Pipe-flow Electrode Derivatives Thiourea Velocity |
| URL | 查看原文 |
| WOS ID | WOS:000228235600003 |
| Citation statistics | |
| Document Type | 期刊论文 |
| Identifier | http://ir.imr.ac.cn/handle/321006/34884 |
| Collection | 中国科学院金属研究所 |
| Recommended Citation GB/T 7714 | X. Jiang,Y. G. Zheng,W. Ke. Corrosion inhibitor performances for carbon dioxide corrosion of N80 steel under static and flowing conditions[J]. Corrosion,2005,61(4):326-334. |
| APA | X. Jiang,Y. G. Zheng,&W. Ke.(2005).Corrosion inhibitor performances for carbon dioxide corrosion of N80 steel under static and flowing conditions.Corrosion,61(4),326-334. |
| MLA | X. Jiang,et al."Corrosion inhibitor performances for carbon dioxide corrosion of N80 steel under static and flowing conditions".Corrosion 61.4(2005):326-334. |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment