Isothermal and thermomechanical fatigue behaviour of a high temperature titanium alloy

IMR OpenIR

	Isothermal and thermomechanical fatigue behaviour of a high temperature titanium alloy
	J. R. Liu; S. X. Li; D. Li; R. Yang
	2004
发表期刊	Materials Science and Technology
ISSN	0267-0836
卷号	20 期号:10 页码:1266-1272
摘要	Isothermal and thermomechanical fatigue (TMF) behaviour (including cyclic stress response and number of cycles to failure) of a Ti-5(.)6Al-4(.)8Sn-2(.)0Zr-1(.)0-Mo-0(.)32Si-0(.)8Nd (wt-%) hightemperature titanium alloy was examined. The purpose of the present investigation was to understand the effect of temperature fluctuation on the cyclic behaviour and fatigue life of this alloy and to test the suitability of lifetime prediction based on isothermal laboratory data. The results indicated that both the level of peak stress and fatigue life were decreasing with increasing test temperature from 400degreesC to 650degreesC in isothermal fatigue (IF) tests. In TMF tests run between 400degreesC and 600degreesC, the peak stresses corresponding to 600degreesC coincide well with that found in IF tests run at 600degreesC, while a slight increase in cyclic hardening was found for peak stress corresponding to 400degreesC compared to that found in a 400degreesC/IF test. This increase in cyclic hardening became more pronounced when the maximum temperature increased to 650degreesC. Fatigue life in 'out of phase' (OP) condition was found to be shorter than under an equivalent 'in phase' (IP) condition, and this gap increased with decreasing mechanical strain amplitude. The results indicate that lifetime prediction based on isothermal laboratory data may lead to non-conservative results if thermal fluctuations are present in components made of the present alloy.
部门归属	chinese acad sci, met res inst, titanium alloy lab, shenyang 110016, peoples r china. chinese acad sci, met res inst, shenyang natl lab mat sci, shenyang 110016, peoples r china.;liu, jr (reprint author), chinese acad sci, met res inst, titanium alloy lab, 72 wenhua rd, shenyang 110016, peoples r china;ryang@imr.ac.cn
关键词	Isothermal And Thermomechanical Fatigue High Temperature Titanium Alloys Fatigue Life Aisi-304l Stainless-steel Imi 834 Deformation-behavior Damage Mechanisms Superalloy Creep
URL	查看原文
WOS记录号	WOS:000225103000011
引用统计	被引频次：3[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/35460
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	J. R. Liu,S. X. Li,D. Li,et al. Isothermal and thermomechanical fatigue behaviour of a high temperature titanium alloy[J]. Materials Science and Technology,2004,20(10):1266-1272.
APA	J. R. Liu,S. X. Li,D. Li,&R. Yang.(2004).Isothermal and thermomechanical fatigue behaviour of a high temperature titanium alloy.Materials Science and Technology,20(10),1266-1272.
MLA	J. R. Liu,et al."Isothermal and thermomechanical fatigue behaviour of a high temperature titanium alloy".Materials Science and Technology 20.10(2004):1266-1272.