Oxidation behavior of a Single-crystal Ni-base superalloy in air. I: At 800 and 900 degrees C

IMR OpenIR

	Oxidation behavior of a Single-crystal Ni-base superalloy in air. I: At 800 and 900 degrees C
	M. H. Li; X. F. Sun; J. G. Li; Z. Y. Zhang; T. Jin; H. R. Guan; Z. Q. Hu
	2003
发表期刊	Oxidation of Metals
ISSN	0030-770X
卷号	59 期号:5-6 页码:591-605
摘要	The oxidation behavior of a Single-crystal Ni-base superalloy was studied using discontinuous thermogravimetric analysis (TGA) and prolonged exposure in air at 800 and 900degreesC. The mass gain of specimens at 900degreesC was found to be lower than that of specimens at 800degreesC because of the formation of a protective inner alpha-Al2O3 layer at 900degreesC. A subparabolic time dependence ( n = 0.16 at 800degreesC and n = 0.10 at 900degreesC) of the oxide growth rate was determined at both temperatures. At 800degreesC, the superalloy exhibited non-uniform oxidation-in some areas a thin scale with an outer NiO layer and an inner layer of an Al-rich oxide was found and, in other areas, complex oxides [CrTaO4, NiCr2O4, (Ni, Co) Al2O4, etc.] below the NiO outer layer formed by growing into the superalloy. The scale formed at 900degreesC is more uniform than that formed at 800degreesC, consisting of several layers: an NiO outer layer, spinel-rich sublayer, a CrTaO4-rich layer, and an alpha-Al2O3 inner layer. The alpha-Al2O3 inner layer provides good oxidation protection and the specimen mass gain is low for test up to 1925 hr.
部门归属	chinese acad sci, inst met res, dept 6, state key lab corros & protect, shenyang 110016, peoples r china.;li, mh (reprint author), chinese acad sci, inst met res, dept 6, state key lab corros & protect, 72 wenhua rd, shenyang 110016, peoples r china
关键词	Single-crystal Ni-base Superalloy Oxidation Kinetics Microstructure Thermal-barrier Coatings Alloys Ma-956 Oxide
URL	查看原文
WOS记录号	WOS:000182606800010
引用统计	被引频次：136[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/35892
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	M. H. Li,X. F. Sun,J. G. Li,et al. Oxidation behavior of a Single-crystal Ni-base superalloy in air. I: At 800 and 900 degrees C[J]. Oxidation of Metals,2003,59(5-6):591-605.
APA	M. H. Li.,X. F. Sun.,J. G. Li.,Z. Y. Zhang.,T. Jin.,...&Z. Q. Hu.(2003).Oxidation behavior of a Single-crystal Ni-base superalloy in air. I: At 800 and 900 degrees C.Oxidation of Metals,59(5-6),591-605.
MLA	M. H. Li,et al."Oxidation behavior of a Single-crystal Ni-base superalloy in air. I: At 800 and 900 degrees C".Oxidation of Metals 59.5-6(2003):591-605.