| Oxidation behavior of Ti3AlC2 at 1000-1400 degrees C in air | |
| X. H. Wang; Y. C. Zhou | |
| 2003 | |
| Source Publication | Corrosion Science
 |
| ISSN | 0010-938X |
| Volume | 45Issue:5Pages:891-907 |
| Abstract | The isothermal oxidation behavior of bulk Ti3AlC2 has been investigated at 1000-1400 degreesC in air for exposure times up to 20 h by means of TGA, XRD, SEM and EDS. It has been demonstrated that Ti3AlC2 has excellent oxidation resistance. The oxidation of Ti3AlC2 generally followed a parabolic rate law with parabolic rate constants, k(p) that increased from 4.1 x 10(-11) to 1.7 x 10(-8) kg(2) m(-4) s(-1) as the temperature increased from 1000 to 1400 degreesC. The scales formed at temperatures below 1300 degreesC were dense, adherent, resistant to cyclic oxidation and layered. The inner layer of these scales formed at temperatures below 1300 degreesC was continuous alpha-Al2O3. The outer layer changed from rutile TiO2 at temperatures below 1200 degreesC to a mixture of Al2TiO5 and TiO2 at 1300 degreesC. In the samples oxidized at 1400 degreesC, the scale consisted of a mixture of Al2TiO5 and, predominantly, alpha-Al2O3, while the adhesion of the scales to the substrates was less than that at the lower temperatures. Effect of carbon monoxide at scale/substrate was involved in the formation of the continuous Al2O3 layers. (C) 2002 Elsevier Science Ltd. All rights reserved. |
| description.department | chinese acad sci, met res inst, shenyang natl lab mat sci, high performance ceram div, shenyang 110016, peoples r china.;zhou, yc (reprint author), chinese acad sci, met res inst, shenyang natl lab mat sci, high performance ceram div, 72 wenhua rd, shenyang 110016, peoples r china |
| Keyword | Ti3alc2 High-temperature Oxidation Continuous Al2o3 Layer Ultra-low Friction Isothermal Oxidation Ti3sic2 Mechanism Stability Carbide Ti2alc Alloys |
| URL | 查看原文 |
| WOS ID | WOS:000180841100004 |
| Citation statistics | |
| Document Type | 期刊论文 |
| Identifier | http://ir.imr.ac.cn/handle/321006/36062 |
| Collection | 中国科学院金属研究所 |
| Recommended Citation GB/T 7714 | X. H. Wang,Y. C. Zhou. Oxidation behavior of Ti3AlC2 at 1000-1400 degrees C in air[J]. Corrosion Science,2003,45(5):891-907. |
| APA | X. H. Wang,&Y. C. Zhou.(2003).Oxidation behavior of Ti3AlC2 at 1000-1400 degrees C in air.Corrosion Science,45(5),891-907. |
| MLA | X. H. Wang,et al."Oxidation behavior of Ti3AlC2 at 1000-1400 degrees C in air".Corrosion Science 45.5(2003):891-907. |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment