	Oxygen Behavior in bulk amorphous Zr-base alloy
	K. Q. Qiu; Q. S. Zhang; A. M. Wang; H. F. Zhang; B. Z. Ding; Z. Q. Hu
	2002
发表期刊	Journal of Materials Science & Technology
ISSN	1005-0302
卷号	18 期号:1 页码:92-94
摘要	Bulk Zr55Al10Ni5Cu30 metallic glass plates with a dimension of 85 mm x 35 mm x 4 mm and a complicated plate were fabricated by injecting casting method using spongy zirconium and industrial purity aluminum, nickel and copper as raw materials. It was shown that the holding time of liquid metals at elevated temperatures had a great influence on the oxygen content of the plates due to the contamination resulting from the atmosphere. Increasing holding time resulted in the increase of oxygen content in the injected alloy. The glass transition temperatures of the bulk metallic glass plates are higher than that reported in the literature and crystallization temperature is lower for the one with higher oxygen content at the same heating rate, The extension of the undercooled liquid region DeltaT(X) reaching about 87 K is 3 K higher than that previously reported and 26 K higher than that with oxygen content of 0.076 wt pct for the one with oxygen content as high as 0.065 wt pct. Therefore the oxygen content of the alloy has a significant influence on the glass forming ability and thermal stability of bulk metal glass. It is suggested that direct correlation between high glass forming ability and large DeltaT(X) is only valid for a well-defined low oxygen concentration or has to be reconsidered by incorporating oxygen as an additional alloying element.
部门归属	chinese acad sci, inst met res, rsa, state key lab, shenyang 110016, peoples r china. liaoning inst technol, jinzhou 211001, peoples r china.;qiu, kq (reprint author), chinese acad sci, inst met res, rsa, state key lab, shenyang 110016, peoples r china
关键词	Zr-base Amorphous Alloy Oxygen Undercooling Zr55al10ni5cu30 Alloy Supercooled Liquid Metallic Glasses Crystallization
URL	查看原文
WOS记录号	WOS:000173663400028
引用统计	被引频次：8[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/36395
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	K. Q. Qiu,Q. S. Zhang,A. M. Wang,et al. Oxygen Behavior in bulk amorphous Zr-base alloy[J]. Journal of Materials Science & Technology,2002,18(1):92-94.
APA	K. Q. Qiu,Q. S. Zhang,A. M. Wang,H. F. Zhang,B. Z. Ding,&Z. Q. Hu.(2002).Oxygen Behavior in bulk amorphous Zr-base alloy.Journal of Materials Science & Technology,18(1),92-94.
MLA	K. Q. Qiu,et al."Oxygen Behavior in bulk amorphous Zr-base alloy".Journal of Materials Science & Technology 18.1(2002):92-94.