| Solid-liquid reaction synthesis and simultaneous densification of polycrystalline Ti2AlC | |
| X. H. Wang; Y. C. Zhou | |
| 2002 | |
| Source Publication | Zeitschrift Fur Metallkunde
 |
| ISSN | 0044-3093 |
| Volume | 93Issue:1Pages:66-71 |
| Abstract | A novel solid-liquid reaction synthesis and simultaneous densification process was developed to fabricate Ti2AlC material using the stoichiometric mixture of Ti, Al and graphite powders as starting materials. This method is a one-step process for the preparation of dense poycrystalline Ti2AlC. Moreover, it provides the advantages of low synthesis temperature, short reaction time and simultaneous synthesis and densification. The microstructure evolution during the high temperature processing was described and the properties of polycrystalline Ti2AlC prepared by this method at 1400 degreesC were investigated. The results showed that Ti2AlC exhibited metallic electrical conductivity and high mechanical properties. The electrical conductivity of Ti2AlC at room temperature was 4.42 x 10(6) Omega(-1) (.) m(-1) and increased with decreasing temperature. The Vickers hardness of Ti2AlC was 2.8 GPa. No indentation cracks were observed and the microdamage is confined in the immediate vicinity of the indent indicating that Ti2AlC is damage tolerant. The flexural strength and the fracture toughness were 275 MPa and 6.5 MPa (.) m(-1/2), respectively. |
| description.department | chinese acad sci, inst met res, ceram & composite dept, shenyang 110016, peoples r china.;zhou, yc (reprint author), chinese acad sci, inst met res, ceram & composite dept, 72,wenhua rd, shenyang 110016, peoples r china |
| Keyword | Solid-liquid Reaction Synthesis Densification Ti2alc Bulk Ceramics Ti3sic2 Damage Hip |
| URL | 查看原文 |
| WOS ID | WOS:000173910600011 |
| Citation statistics | |
| Document Type | 期刊论文 |
| Identifier | http://ir.imr.ac.cn/handle/321006/36442 |
| Collection | 中国科学院金属研究所 |
| Recommended Citation GB/T 7714 | X. H. Wang,Y. C. Zhou. Solid-liquid reaction synthesis and simultaneous densification of polycrystalline Ti2AlC[J]. Zeitschrift Fur Metallkunde,2002,93(1):66-71. |
| APA | X. H. Wang,&Y. C. Zhou.(2002).Solid-liquid reaction synthesis and simultaneous densification of polycrystalline Ti2AlC.Zeitschrift Fur Metallkunde,93(1),66-71. |
| MLA | X. H. Wang,et al."Solid-liquid reaction synthesis and simultaneous densification of polycrystalline Ti2AlC".Zeitschrift Fur Metallkunde 93.1(2002):66-71. |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment