| Oxidation behavior of Ti3AlC2 powders in flowing air | |
| X. H. Wang; Y. C. Zhou | |
| 2002 | |
| Source Publication | Journal of Materials Chemistry
 |
| ISSN | 0959-9428 |
| Volume | 12Issue:9Pages:2781-2785 |
| Abstract | The oxidation behavior of Ti3AlC2 powders has been investigated in air by means of simultaneous TGA-DSC, XRD, Raman spectra, SEM, EDS and BET specific surface measurement to understand the intrinsic oxidation behavior of this newly developed ternary compound. The starting and complete oxidation temperatures determined by simultaneous TGA-DSC were 400 and 1120 degreesC, respectively. These temperatures are higher than those for TiC, suggesting that Ti3AlC2 is more oxidation resistant than TiC. An anomalous oxidation temperature range of 550-650 degreesC in which the final mass gains due to the isothermal oxidation of Ti3AlC2 powders at 550, 600 and 650 degreesC for 2 h are significantly greater than that at a higher temperature of 700 degreesC, was observed. This anomalous oxidation behavior suggests that direct reaction dominated with high oxidation kinetics in this temperature range, which was confirmed by SEM morphology observation and BET specific surface area measurement. The oxidation of Ti3AlC2 powders at temperatures below 700 degreesC resulted in two modifications of TiO2 (anatase and rutile). At temperatures above 800 degreesC the oxidation products consisted of rutile TiO2 and alpha-Al2O3. |
| description.department | chinese acad sci, high performance ceram div, shenyang natl lab mat sci, inst met res, shenyang 110016, peoples r china.;zhou, yc (reprint author), chinese acad sci, high performance ceram div, shenyang natl lab mat sci, inst met res, 72 wenhua rd, shenyang 110016, peoples r china |
| Keyword | Ti3sic2 Carbide Microscopy Ti2alc |
| URL | 查看原文 |
| WOS ID | WOS:000177941100037 |
| Citation statistics | |
| Document Type | 期刊论文 |
| Identifier | http://ir.imr.ac.cn/handle/321006/36443 |
| Collection | 中国科学院金属研究所 |
| Recommended Citation GB/T 7714 | X. H. Wang,Y. C. Zhou. Oxidation behavior of Ti3AlC2 powders in flowing air[J]. Journal of Materials Chemistry,2002,12(9):2781-2785. |
| APA | X. H. Wang,&Y. C. Zhou.(2002).Oxidation behavior of Ti3AlC2 powders in flowing air.Journal of Materials Chemistry,12(9),2781-2785. |
| MLA | X. H. Wang,et al."Oxidation behavior of Ti3AlC2 powders in flowing air".Journal of Materials Chemistry 12.9(2002):2781-2785. |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment