Self-similarity of the crack front in stress corrosion fracture

IMR OpenIR

	Self-similarity of the crack front in stress corrosion fracture
	J. Deng; Q. Y. Long; C. W. Lung
	2001
发表期刊	Journal of Materials Science & Technology
ISSN	1005-0302
卷号	17 页码:S69-S72
摘要	In this letter, a new method was proposed to visualize the crack front in stress corrosion fracture of high strength steel. The fractal characteristic of the crack front was analyzed by measuring its fractal dimension and roughness exponent at the same time. The experimental results show that the irregularity of the crack front was partly self-affine.
部门归属	chinese acad sci, inst met res, int ctr mat phys, shenyang 110016, peoples r china.;deng, j (reprint author), chinese acad sci, inst met res, int ctr mat phys, shenyang 110016, peoples r china;qwlong@imr.ac.cn
关键词	Porous-media Roughness Model
URL	查看原文
WOS记录号	WOS:000172126300016
引用统计
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/36627
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	J. Deng,Q. Y. Long,C. W. Lung. Self-similarity of the crack front in stress corrosion fracture[J]. Journal of Materials Science & Technology,2001,17:S69-S72.
APA	J. Deng,Q. Y. Long,&C. W. Lung.(2001).Self-similarity of the crack front in stress corrosion fracture.Journal of Materials Science & Technology,17,S69-S72.
MLA	J. Deng,et al."Self-similarity of the crack front in stress corrosion fracture".Journal of Materials Science & Technology 17(2001):S69-S72.