The structure and magnetic properties of Nd8Fe84-xCuxTi8 (x=0 similar to 3) alloys prepared by mechanical alloying

IMR OpenIR

	The structure and magnetic properties of Nd8Fe84-xCuxTi8 (x=0 similar to 3) alloys prepared by mechanical alloying; The structure and magnetic properties of Nd8Fe84-xCuxTi8 (x=0 similar to 3) alloys prepared by mechanical alloying
	B. Z. Cui; X. K. Sun; W. Liu; D. Y. Geng; Z. D. Zhang; X. G. Zhao
	2000 ; 2000
发表期刊	Journal of Alloys and Compounds ; Journal of Alloys and Compounds
ISSN	0925-8388 ; 0925-8388
卷号	297 期号:1-2 页码:219-225
摘要	The effects of a partial substitution of Cu for Fe on the structure and magnetic properties of mechanically alloyed Nd8Fe84Ti8 alloys were studied in detail. Compared with Cu-free Nd8Fe84Ti8 alloys prepared by mechanical alloying under the same conditions, the temperature necessary for the formation of the Nd(Fe, Ti)(12) phase decreased from 900 to 750 degrees C with the addition of 3 at.% Cu. The addition of Cu negatively influenced the nitrogenation of the Nd(Fe, Ti)(12) phase. The pretreatment of hydrogenation on the Cu-added alloys at 300 degrees C facilitated the formation of nitrides. With increasing the annealing temperature, the intrinsic coercivity of the nitrides increased until it attained a maximum at 850 degrees C. In the 1 at.% Cu-added alloys annealed at temperatures between 750 and 800 degrees C, the metastable phase Nd(Fe, Ti)(7) was formed. With increasing the annealing temperature, the Nd(Fe, Ti)(7) phase was gradually transformed into the Nd(Fe, Ti)(12) phase. The intrinsic coercivity of the 1 at.% Cu-added nitrides reached a maximum at 900 degrees C. With increasing Cu content, the magnetic properties of the nitrides degraded. (C) 2000 Elsevier Science S.A. All rights reserved.; The effects of a partial substitution of Cu for Fe on the structure and magnetic properties of mechanically alloyed Nd8Fe84Ti8 alloys were studied in detail. Compared with Cu-free Nd8Fe84Ti8 alloys prepared by mechanical alloying under the same conditions, the temperature necessary for the formation of the Nd(Fe, Ti)(12) phase decreased from 900 to 750 degrees C with the addition of 3 at.% Cu. The addition of Cu negatively influenced the nitrogenation of the Nd(Fe, Ti)(12) phase. The pretreatment of hydrogenation on the Cu-added alloys at 300 degrees C facilitated the formation of nitrides. With increasing the annealing temperature, the intrinsic coercivity of the nitrides increased until it attained a maximum at 850 degrees C. In the 1 at.% Cu-added alloys annealed at temperatures between 750 and 800 degrees C, the metastable phase Nd(Fe, Ti)(7) was formed. With increasing the annealing temperature, the Nd(Fe, Ti)(7) phase was gradually transformed into the Nd(Fe, Ti)(12) phase. The intrinsic coercivity of the 1 at.% Cu-added nitrides reached a maximum at 900 degrees C. With increasing Cu content, the magnetic properties of the nitrides degraded. (C) 2000 Elsevier Science S.A. All rights reserved.
部门归属	acad sinica, inst met res, shenyang 110015, peoples r china.;cui, bz (reprint author), acad sinica, inst met res, shenyang 110015, peoples r china ; acad sinica, inst met res, shenyang 110015, peoples r china.;cui, bz (reprint author), acad sinica, inst met res, shenyang 110015, peoples r china
关键词	Nd(Fe Nd(Fe Ti)(12) Cu Addition Ti)(12) Cu Addition Mechanical Alloying Mechanical Alloying Magnetic Properties Magnetic Properties Evolution Evolution Nitrides Nitrides
URL	查看原文 ; 查看原文
WOS记录号	WOS:000084513000037 ; WOS:000084513000037
引用统计	被引频次：2[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/37012
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	B. Z. Cui,X. K. Sun,W. Liu,et al. The structure and magnetic properties of Nd8Fe84-xCuxTi8 (x=0 similar to 3) alloys prepared by mechanical alloying, The structure and magnetic properties of Nd8Fe84-xCuxTi8 (x=0 similar to 3) alloys prepared by mechanical alloying[J]. Journal of Alloys and Compounds, Journal of Alloys and Compounds,2000, 2000,297, 297(1-2):219-225, 219-225.
APA	B. Z. Cui,X. K. Sun,W. Liu,D. Y. Geng,Z. D. Zhang,&X. G. Zhao.(2000).The structure and magnetic properties of Nd8Fe84-xCuxTi8 (x=0 similar to 3) alloys prepared by mechanical alloying.Journal of Alloys and Compounds,297(1-2),219-225.
MLA	B. Z. Cui,et al."The structure and magnetic properties of Nd8Fe84-xCuxTi8 (x=0 similar to 3) alloys prepared by mechanical alloying".Journal of Alloys and Compounds 297.1-2(2000):219-225.