Failure behavior of an aluminide coating on a co-base superalloy during high-temperature oxidation in air

IMR OpenIR

	Failure behavior of an aluminide coating on a co-base superalloy during high-temperature oxidation in air
	P. S. Liu; K. M. Liang; S. R. Gu
	2000
发表期刊	Oxidation of Metals
ISSN	0030-770X
卷号	54 期号:3-4 页码:277-283
摘要	A surface-morphology change has been observed for an aluminide coating on the Go-base superalloy DZ40M during oxidation at 1100 degrees C in air. The oxide formed on the coating remained an even greyish-white color during the stable oxidation stage, whereas, dark-colored corrosion nodules were observed when oxidation of the coating accelerated. The number of nodules increased with time, along with growth of the nodules, eventually covering the entire surface which signified failure.
部门归属	tsing hua univ, dept mat sci & engn, beijing 100084, peoples r china. chinese acad sci, inst met res, shenyang 110015, peoples r china.;liu, ps (reprint author), tsing hua univ, dept mat sci & engn, beijing 100084, peoples r china
关键词	Aluminide Coating Co-base Superalloy High-temperature Oxidation Corrosion Nodule
URL	查看原文
WOS记录号	WOS:000088799600005
引用统计	被引频次：13[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/37102
专题	中国科学院金属研究所
推荐引用方式 GB/T 7714	P. S. Liu,K. M. Liang,S. R. Gu. Failure behavior of an aluminide coating on a co-base superalloy during high-temperature oxidation in air[J]. Oxidation of Metals,2000,54(3-4):277-283.
APA	P. S. Liu,K. M. Liang,&S. R. Gu.(2000).Failure behavior of an aluminide coating on a co-base superalloy during high-temperature oxidation in air.Oxidation of Metals,54(3-4),277-283.
MLA	P. S. Liu,et al."Failure behavior of an aluminide coating on a co-base superalloy during high-temperature oxidation in air".Oxidation of Metals 54.3-4(2000):277-283.